Coated positive electrode active material, positive electrode for nonaqueous secondary battery, nonaqueous secondary battery, and their production methods
Disclosed is a nonaqueous secondary battery ( 100 ) comprising a positive electrode ( 155 ) having a positive current collector ( 151 ) made of a metal, and a positive electrode active material ( 153 ) composed of a lithium-metal complex oxide. The surface of the positive electrode active material ( 153 ) is coated with a lithium salt ( 158 ) having an average thickness of 20-50 nm.
1. A method of producing a coated positive electrode active material in which a positive electrode active material made of lithium-metal complex oxide has a surface coated with a coating of lithium salt containing lithium carbonate and having an average thickness of 20 to 50 nm, the method comprising:
a first firing step of firing a raw material for the positive electrode active material in a reaction system having an oxygen atmosphere; and
a second firing step, following the first firing step, of supplying CO 2 gas into the reaction system having the oxygen atmosphere and firing the raw material in the reaction system having the oxygen atmosphere containing CO 2 at a higher concentration than in the first firing step,
the second firing step including firing the raw material for 4 to 8 hours in an oxygen atmosphere at a CO 2 concentration of 300 to 400 ppm to form the coating of lithium salt having an average thickness of 20 to 50 nm on the surface of the positive electrode active material.
2. A method of producing a coated positive electrode active material in which a positive electrode active material made of lithium-metal complex oxide has a surface coated with a coating of lithium salt containing lithium carbonate and having an average thickness of 20 to 50 nm, the method comprising:
exposing the positive electrode active material to an atmosphere of constant temperature and constant humidity with a CO 2 gas concentration of 300 to 400 ppm, a temperature of 30 to 80° C., and a relative humidity of 40 to 100% RH to form the coating of lithium salt having an average thickness of 20 to 50 nm on the surface of the positive electrode active material.
3. A method of producing a positive electrode for nonaqueous secondary battery, comprising:
producing a coated positive electrode active material in which a positive electrode active material made of lithium-metal complex oxide has a surface coated with a coating of lithium salt containing lithium carbonate and having an average thickness of 20 to 50 nm, including:
a first firing step of firing a raw material for the positive electrode active material in a reaction system having an oxygen atmosphere; and
a second firing step, following the first firing step, of supplying CO 2 gas into the reaction system having the oxygen atmosphere and firing the raw material in the reaction system having the oxygen atmosphere containing CO 2 at a higher concentration than in the first firing step,
the second firing step including firing the raw material for 4 to 8 hours in an oxygen atmosphere at a CO 2 concentration of 300 to 400 ppm to form the coating of lithium salt having an average thickness of 20 to 50 nm on the surface of the positive electrode active material; and
applying a positive paste on a positive current collector made of metal, the positive paste being prepared by mixing at least binder resin, water, and the coated positive electrode active material.
4. A method of producing a nonaqueous secondary battery including a positive electrode for nonaqueous secondary battery, the method comprising:
producing the positive electrode, including
producing a coated positive electrode active material in which a positive electrode active material made of lithium-metal complex oxide has a surface coated with a coating of lithium salt containing lithium carbonate and having an average thickness of 20 to 50 nm, including:
a first firing step of firing a raw material for the positive electrode active material in a reaction system having an oxygen atmosphere; and
a second firing step, following the first firing step, of supplying CO 2 gas into the reaction system having the oxygen atmosphere and firing the raw material in the reaction system having the oxygen atmosphere containing CO 2 at a higher concentration than in the first firing step,
the second firing step including firing the raw material for 4 to 8 hours in an oxygen atmosphere at a CO 2 concentration of 300 to 400 ppm to form the coating of lithium salt having an average thickness of 20 to 50 nm on the surface of the positive electrode active material; and
applying a positive paste on a positive current collector made of metal, the positive paste being prepared by mixing at least binder resin, water, and the coated positive electrode active material; and
producing a negative electrode.
5. A method of producing a positive electrode for nonaqueous secondary battery, comprising:
producing a coated positive electrode active material in which a positive electrode active material made of lithium-metal complex oxide has a surface coated with a coating of lithium salt containing lithium carbonate and having an average thickness of 20 to 50 nm, including
exposing the positive electrode active material to an atmosphere of constant temperature and constant humidity with a CO 2 gas concentration of 300 to 400 ppm, a temperature of 30 to 80° C., and a relative humidity of 40 to 100% RH to form the coating of lithium salt having an average thickness of 20 to 50 nm on the surface of the positive electrode active material; and
applying a positive paste on a positive current collector made of metal, the positive paste being prepared by mixing at least binder resin, water, and the coated positive electrode active material.
6. A method of producing a nonaqueous secondary battery including a positive electrode for nonaqueous secondary battery, the method comprising:
producing the positive electrode including
producing a coated positive electrode active material in which a positive electrode active material made of lithium-metal complex oxide has a surface coated with a coating of lithium salt containing lithium carbonate and having an average thickness of 20 to 50 nm, including
exposing the positive electrode active material to an atmosphere of constant temperature and constant humidity with a CO 2 gas concentration of 300 to 400 ppm, a temperature of 30 to 80° C., and a relative humidity of 40 to 100% RH to form the coating of lithium salt having an average thickness of 20 to 50 nm on the surface of the positive electrode active material; and
applying a positive paste on a positive current collector made of metal, the positive paste being prepared by mixing at least binder resin, water, and the coated positive electrode active material; and
producing a negative electrode.