Hydraulic binder with low clinker content
A hydraulic binder includes, in parts by mass: (a) from 20 to 60 parts of Portland clinker; (b) from 20 to 40 parts of slag; and (c) from 0 to 60 parts of inorganic material other than the clinker and the slag; the sum of (a), (b) and (c) being equal to 100 parts; which binder further includes a slag activator including, relative to 100 parts of the sum of (a) and (b): from 1.4 to 6.55 parts of alkali metal salt, expressed as equivalent-Na 2 O; and from 1.1 to 11.0 parts of calcium sulfate, expressed as SO 3 .
1. Hydraulic binder comprising, in parts by mass:
(a) from 20 to 60 parts of Portland clinker;
(b) from 20 to 40 parts of slag;
(c) greater than 0 and up to 60 parts of inorganic material other than the clinker and the slag; the inorganic material comprising a pozzolan, calcined shale, calcium carbonate, silica fume, metakaolin or a mixture thereof;
the sum of (a), (b) and (c) being equal to 100 parts; and
a slag activator comprising, relative to 100 parts of the sum of (a) and (b):
from 1.4 to 6.55 parts of alkali metal salt, expressed as equivalent-Na 2 O; and from 1.1 to 11.0 parts of calcium sulfate, expressed as SO 3 ;
which binder comprises no fly ash,
wherein the inorganic material is made of particles having a Dv90 less than or equal to 200 μm, wherein Dv90 is the 90 th percentile of the size distribution of the particles of the inorganic material, by volume.
2. A hydraulic binder according to claim 1 , wherein the Blaine specific surface of the Portland clinker is greater than or equal to 5500 cm 2 /g.
3. A hydraulic binder according to claim 1 , wherein the alkali metal salt is sodium sulfate.
4. A hydraulic binder according to claim 1 , wherein the inorganic material comprises calcium carbonate.
5. A hydraulic binder according to claim 1 , comprising no alkali metal hydroxide.
6. A hydraulic composition comprising a hydraulic binder according to claim 1 , aggregate and water.
7. A process for preparing a hydraulic composition according to claim 6 , which process comprises mixing a hydraulic binder according to claim 1 , aggregate and water.
8. A shaped article for the construction field comprising a hydraulic binder according to claim 1 .
9. A hydraulic binder according to claim 1 , wherein the amount of slag is from 20 to 35 parts.
10. A hydraulic binder according to claim 1 , wherein the slag has a blain specific surface greater than or equal to 3000 cm 2 /g.
11. A hydraulic binder according to claim 1 , wherein the amount of the inorganic material is from 5 to 60 parts.
12. A hydraulic binder according to claim 11 , wherein the amount of the inorganic material is from 10 to 60 parts.
13. A hydraulic binder according to claim 1 , wherein the inorganic material is made of particles having a Dv97 less than or equal to 200 μm, wherein Dv97 is the 97 th percentile of the size distribution of the particles of the inorganic material, by volume.
14. A hydraulic binder according to claim 1 , wherein the amount of alkali metal salt is from 2 to 5.5 parts.
15. A hydraulic binder according to claim 14 , wherein the amount of alkali metal salt is from 2.5 to 4.5 parts.
16. A process comprising increasing the compressive strength 24 hours after mixing and/or 28 days after mixing of a hydraulic composition which comprises aggregate, water and a hydraulic binder comprising, in parts by mass:
(a) from 20 to 60 parts of Portland clinker;
(b) from 20 to 40 parts of slag; and
(c) greater than 0 and up to 60 parts of inorganic material other than the clinker and the slag; the inorganic material comprising a pozzolan, calcined shale, calcium carbonate, silica fume, metakaolin or a mixture thereof;
the sum of (a), (b) and (c) being equal to 100 parts;
which binder comprises no fly ash;
with a slag activator comprising 1.4 to 6.55 parts of alkali metal salt, expressed as equivalent-Na 2 O, and 1.1 to 11.0 parts of calcium sulfate, expressed as SO 3 all parts being by mass and relative to 100 parts of Portland clinker and of slag,
wherein the inorganic material is made of particles having a Dv90 less than or equal to 200 μm, wherein Dv90 is the 90 th percentile of the size distribution of the particles of the inorganic material, by volume.
17. A process according to claim 16 , wherein the amount of the inorganic material is from 5 to 60 parts.
18. A process according to claim 17 , wherein the amount of the inorganic material is from 10 to 60 parts.
19. A process according to claim 16 , wherein the inorganic material is made of particles having a Dv97 less than or equal to 200 μm, wherein Dv97 is the 97 th percentile of the size distribution of the particles of the inorganic material, by volume.
20. A process according to claim 16 , wherein the Blaine specific surface of the Portland clinker is greater than or equal to 5500 cm 2 /g.