Metal material with a bismuth film attached and method for producing same, surface treatment liquid used in said method, and cationic electrodeposition coated metal material and method for producing same
A metal material is provided with a bismuth coating which enables the subsequent coating to be accomplished at a high throwing power, and has excellent corrosion resistance, coating adhesion and is able to be produced with reduced damage to the environment. The metal material has a surface and a bismuth-containing layer deposited on at least a part of the surface of the metal material, wherein the percentage of bismuth atoms in the number of atoms in the surface layer of the metal material with a bismuth coating is at least 10%.
1. A surface treating solution for use in a chemical conversion of a metal material surface conducted as a pretreatment of a coating, wherein the surface treating solution contains bismuth ions and a first ligand for the bismuth ions in an amount effective to form a bismuth chemical conversion film on the metal surface.
2. The surface treating solution according to claim 1 , wherein said coating is by cationic electrodeposition.
3. The surface treating solution according to claim 1 , further comprising a brightener.
4. The surface treating solution according to claim 3 , wherein the brightener is an organic compound having at least one member selected from the group consisting of an aromatic ring, a sulfone group, a formyl group, a carboxy group and an amino group.
5. The surface treating solution according to claim 3 , wherein the solution at the time of the surface treatment contains the brightener at a weight concentration of 10 to 10,000 ppm.
6. The surface treating solution according to claim 3 , wherein the first ligand is at least one member selected from the group consisting of an minopolycarboxylic acid and a carboxylic acid, and the solution contains at least one ligand which has a stability for the bismuth ions higher than a stability for an ion of a metal constituting the metal material.
7. The surface treating solution according to claim 3 , wherein
the first ligand is at least one member selected from the group consisting of an aminopolycarboxylic acid and/e a carboxylic acid, and has a stability for the bismuth ions higher than a stability for an ion of a metal constituting the metal material, and
the solution further comprises a second ligand which has a stability for the ion of the metal constituting the metal material higher than a stability for the bismuth ions.
8. The surface treating solution according to claim 3 , wherein the solution at the time of the surface treatment contains the bismuth ions at a weight concentration of 5 to 1,000 ppm.
9. The surface treating solution according to claim 3 , having a pH of at least 2 and less than 10.5.
10. The surface treating solution according to claim 1 , wherein the first ligand is at least one member selected from the group consisting of an aminopolycarboxylic acid and a carboxylic acid, and the solution contains at least one ligand which has a stability for the bismuth ions higher than a stability for an ion of a metal constituting the metal material.
11. The surface treating solution according to claim 1 , wherein,
the first ligand is an aminopolycarboxylic acid and has a stability for the bismuth ions higher than a stability for an ion of a metal constituting the metal material; and
the solution further comprises a second ligand which has a stability for the ion of a metal constituting the metal material higher than a stability for the bismuth ions.
12. The surface treating solution according to claim 1 , wherein the solution at the time of the surface treatment contains the bismuth ions at a weight concentration of 5 to 1,000 ppm.
13. The surface treating solution according to claim 12 , wherein the solution at the time of the surface treatment contains the first ligand at a weight concentration of 5 to 25,000 ppm.
14. The surface treating solution according to claim 1 , having a pH of at least 2 and less than 10.5.