High-density polyethylene compositions, method of producing the same, closure devices made therefrom, and method of making such closure devices
The instant invention is a high-density polyethylene composition, method of producing the same, closure devices made therefrom, and method of making such closure devices. The high-density polyethylene composition according to the present invention comprises (a) a first component comprising a high molecular weight ethylene alpha-olefin copolymer having a density in the range of 0.927 to 0.938 g/cm3, and a melt flow rate (I21) in the range of 4 to 10 g/10 minutes, and (b) a second component comprising a low molecular weight ethylene polymer having a density in the range of 0.960 to 0.975 g/cm3, and a melt index (I2) in the range of 100 to 1200 g/10 minutes; and wherein the high-density polyethylene composition has a melt index (I2) in the range of from 2 to 10 g/10 minutes, a density in the range of from 0.950 to 0.960 g/cm3, and a flow direction shrinkage to cross flow direction shrinkage ratio in the range of from 2 to 3.2, and an environmental stress crack resistance (ESCR) (F50) according to ASTM D-1693, condition B at 50° C., and using 10 percent Branched Octylphenoxy Poly(Ethyleneoxy) Ethanol, in the range of equal to or greater than 50 hours.
1. A high-density polyethylene composition comprising:
a first component comprising a high molecular weight ethylene alpha-olefin copolymer having a density in the range of 0.930 to 0.935 g/cm 3 , and a melt flow rate (I 21 ) in the range of 4 to 9 g/10 minutes; and
a second component comprising a low molecular weight ethylene polymer having a density in the range of 0.960 to 0.973 g/cm 3 ;
wherein said high-density polyethylene composition has a melt index (I 2 ) in the range of from 2 to 5 g/10 minutes, a density in the range of from 0.950 to 0.960 g/cm 3 , and a flow direction shrinkage to cross flow direction shrinkage ratio after 48 hours in the range of from 2 to 3.0, and an environmental stress crack resistance (ESCR) (F50) according to ASTM D-1693, condition B at 50° C., and using 10 percent Branched Octylphenoxy Poly(Ethyleneoxy) Ethanol, in the range of equal to or greater than 50 hours.
2. A closure device comprising:
a high-density polyethylene composition comprising:
a first component comprising a high molecular weight ethylene alpha-olefin copolymer having a density in the range of 0.930 to 0.935 g/cm 3 , and a melt flow rate (I 21 ) in the range of 4 to 9 g/10 minutes; and
a second component comprising a low molecular weight ethylene polymer having a density in the range of 0.960 to 0.973 g/cm 3 ;
wherein said high-density polyethylene composition has a melt index (I 2 ) in the range of from 2 to 5 g/10 minutes, a density in the range of from 0.950 to 0.960 g/cm 3 , and a flow direction shrinkage to cross flow direction shrinkage ratio after 48 hours in the range of from 2 to 3.0, and an environmental stress crack resistance (ESCR) (F50) according to ASTM D-1693, condition B at 50° C., and using 10 percent Branched Octylphenoxy Poly(Ethyleneoxy) Ethanol, in the range of equal to or greater than 50 hours.
3. The high-density polyethylene composition according to claim 1 , wherein said high-density polyethylene composition has a melt flow ratio (I 21 /I 2 ) of less than 60.
4. The high-density polyethylene composition according to claim 1 , wherein said first component has a molecular weight, Mw, in the range of from 140,000 to 200,000.
5. The high-density polyethylene composition according to claim 1 , wherein said second component has a molecular weight, Mw, in the range of from 10,000 to 30,000.
6. The high-density polyethylene composition according to claim 1 , wherein the high-density polyethylene composition has a high load melt index (I 21 ) from 89.6 to 120.9, a melt flow ratio (I 21 /I 2 ) from 31 to 47.
7. The closure device according to claim 2 , wherein the high-density polyethylene composition has a high load melt index (I 21 ) from 89.6 to 120.9, a melt flow ratio (I 21 /I 2 ) from 31 to 47.