Method of producing tempered glass sheet
Provided is a method of producing a tempered glass sheet, comprising applying tempering treatment to a glass sheet by increasing the content of SiO 2 in terms of mass in a surface region of a glass sheet through application of thermal treatment to the glass sheet to 1.03 or more times that in an interior region positioned at a depth of 1 μm from a surface of the glass sheet.
1. A method of producing a tempered glass sheet, comprising:
forming a glass sheet having, as a glass composition in terms of mass %, 50% to 68% of SiO 2 , 10% to 25% of Al 2 O 3 , 3% to 20% of B 2 O 3 , 0% to 10% of MgO, 3% to 15% of CaO, 0% to 10% of BaO, and 0% to 10% of SrO; and
tempering the formed glass sheet by increasing a content of SiO 2 in terms of mass in a surface region of the glass sheet by volatilizing glass components through a thermal treatment which is carried out successively after forming the glass sheet to 1.03 or more times that in an interior region positioned at a depth of 1 μm from a surface of the glass sheet,
wherein the thermal treatment consists of heating the glass sheet at a temperature of 800 to 1,000° C. for 30 seconds to 5 hours.
2. The method according to claim 1 , wherein the tempered glass sheet has an unpolished surface.
3. The method according to claim 1 , wherein the tempered glass sheet is substantially free of alkali metal oxides.