Phosphor composition, light emitting device, and the method of preparing the phosphor composition
There are provided a phosphor and a light emitting device. The phosphor includes a phosphor composition including a rare-earth element employed in a compound represented by the equation: L 3 Si 6 N 11 , wherein L is one or more elements selected from La, Y, Gd and Lu, the rare-earth element is one or more elements selected from Mn, Ce, Pr, Nd, Sm, Eu, Gd, Dy, Tb, Ho, Er, Tm and Yb. The phosphor composition is provided in particle form. The particle has at least a portion of a plane perpendicular to a [001] direction to be flat thereon so as to have a crystal plane.
1. A phosphor composition comprising:
a rare-earth element or manganese (Mn) employed in a compound represented by the following equation:
L 3 Si 6 N 11 ,
L being one or more elements selected from a group consisting of lanthanum (La), yttrium (Y), gadolinium (Gd) and lutetium (Lu),
the rare-earth element selected from one or more of: cerium (Ce), praseodymium (Pr), neodymium (Nd), samarium (Sm), europium (Eu), gadolinium (Gd), dysprosium (Dy), terbium (Tb), holmium (Ho), erbium (Er), thulium (Tm), and ytterbium (Yb),
wherein the composition is in a particle form, the particle having at least a portion of a plane perpendicular to a [001] direction to be flat thereon so as to have a crystal plane.
2. The phosphor composition of claim 1 , wherein the particle has a flat shape in which 50% or more of the plane thereof perpendicular to the [001] direction has the crystal plane.
3. The phosphor composition of claim 1 , wherein the particle has a flat shape in which at least a portion of a plane perpendicular to another direction different from the [100] direction has the crystal plane.
4. The phosphor composition of claim 3 , wherein in the particle, a ratio of a length of the plane thereof perpendicular to the [001] direction to that of the plane perpendicular to another direction, different from the [001] direction ranges from 1:3 to 3:1.
5. The phosphor composition of claim 1 , wherein the compound includes the rare-earth element, and the rare-earth element is Ce or Eu.
6. The phosphor composition of claim 1 , wherein a central wavelength from a light emission spectrum of the phosphor is 520 nm or more when ultraviolet light or blue light is used as an excitation source.
7. A light emitting device comprising:
a light emitting device emitting excitation light; and
a wavelength conversion unit absorbing the excitation light to emit visible light,
the wavelength conversion unit including a phosphor composition, the phosphor composition including:
a rare-earth element or manganese (Mn) employed in a compound represented the following equation:
L 3 Si 6 N 11 ,
L being one or more elements selected from a group consisting of lanthanum (La), yttrium (Y), gadolinium (Gd) and lutetium (Lu),
the rare-earth element selected from one or more of: cerium (Ce), praseodymium (Pr), neodymium (Nd), samarium (Sm), europium (Eu), gadolinium (Gd), dysprosium (Dy), terbium (Tb), holmium (Ho), erbium (Er), thulium (Tm), and ytterbium (Yb),
wherein the phosphor composition is in particle form, the particle having at least a portion of a plane perpendicular to a [001] direction to be flat thereon so as to have a crystal plane.
8. The light emitting device of claim 7 , wherein the light emitting device is an ultraviolet light emitting diode or a blue light emitting diode.
9. The light emitting device of claim 7 , wherein the particle has a flat shape in which 50% or more of the plane thereof perpendicular to the [001] direction has the crystal plane.
10. The light emitting device of claim 7 , wherein the particle has the flat shape in which at least a portion of a plane perpendicular to another direction different from the [100] direction has the crystal plane.
11. The light emitting device of claim 10 , wherein the particle has a ratio of 1:3 to 3:1 in a length of the plane perpendicular to the [001] direction to that of the plane perpendicular to the direction different from the [001] direction.
12. A method of preparing a phosphor composition, the method comprising steps of:
mixing a Si raw material, an L element, and a rare-earth element or manganese (Mn) to form a mixture, wherein:
the rare-earth element is employed in a compound represented the following equation:
L 3 Si 6 N 11 ,
the L element selected from a group consisting of lanthanum (La), yttrium (Y), gadolinium (Gd) and lutetium (Lu),
the rare-earth element selected from one or more of: cerium (Ce), praseodymium (Pr), neodymium (Nd), samarium (Sm), europium (Eu), gadolinium (Gd), dysprosium (Dy), terbium (Tb), holmium (Ho), erbium (Er), thulium (Tm), and ytterbium (Yb),
at least one of the Si raw material and the L element including nitrogen (N); and
synthesizing the mixture to form the L 3 Si 6 N 11 compound in a H 2 /N 2 mixture gas atmosphere at a temperature of about 1600° C. for about 10 hours.
13. The method of claim 12 , further comprising the step of:
providing BaF 2 as a flux during the synthesizing step.
14. The method of claim 12 , wherein the mixing step is performed in an argon-substituted glove box.
15. The method of claim 12 , wherein the phosphor composition is in particle form.
16. The method of claim 12 , wherein:
the mixing includes mixing the Si raw material, the L element, and the rare-earth element, and the rare-earth element is Ce or Eu, and
the Si raw material is Si 3 N 4 .