Dip-formed synthetic polyisoprene latex articles with improved intraparticle and interparticle crosslinks
A synthetic polyisoprene latex emulsion has pre-vulcanization composition and post vulcanization composition. The pre-vulcanization composition comprises soluble sulfur with high S 8 ring structure that is catalytically broken by a zinc dithiocarbamate. Surfactants present in the pre-vulcanization composition wets synthetic polyisoprene particles and permeates small sized sulfur and accelerator molecules into the interior of these particles thereby pre-vulcanizing the particles. The degree of pre-vulcanization is verified by isopropanol index test. The latex emulsion has post-vulcanization composition with accelerators that crosslink inter-particle region during post vulcanization cure cycle. The dipped synthetic polyisoprene article is substantially uniformly cured both in the inter-particle and intra-particle regions and reliably exhibits high cross link density, uniform distribution of double bonds in TEM and zinc segregation at the boundaries or original particles by electron microprobe analysis. The films exhibit high tensile strength, tensile modulus, tear strength, burst pressure and burst volume.
1. A synthetic, dip-formed polyisoprene elastomeric condom comprising:
synthetic polyisoprene particles, said synthetic polyisoprene particles bonded to each other through intra-polyisoprene particle crosslinks and inter-polyisoprene particle crosslinks;
wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8000 g/mol between the crosslinks.
2. A condom of claim 1 , wherein the condom has an elongation at break of at least 945%.
3. The condom of claim 2 , wherein the condom exhibits a fracture surface with an absence of scanning electron microscope-viewable intra-polyisoprene particle and inter-polyisoprene particle features when ruptured at room temperature.
4. A condom of claim 2 , wherein the condom has a tensile strength of at least 30 MPa.
5. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 7500 g/mol between the crosslinks.
6. The condom of claim 5 , wherein the condom has an elongation at break of at least 945%.
7. The condom of claim 6 , wherein the condom exhibits a fracture surface with an absence of scanning electron microscope-viewable intra-polyisoprene particle and inter-polyisoprene particle features when ruptured at room temperature.
8. The condom of claim 6 , wherein the condom has a tensile strength of at least 30 MPa.
9. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 7000 g/mol between the crosslinks.
10. The condom of claim 9 , wherein the condom has an elongation at break of at least 945%.
11. The condom of claim 10 , wherein the condom exhibits a fracture surface with an absence of scanning electron microscope-viewable intra-polyisoprene particle and inter-polyisoprene particle features when ruptured at room temperature.
12. The condom of claim 10 , wherein the condom has a tensile strength of at least 30 MPa.
13. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8900 g/mol between the crosslinks.
14. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8800 g/mol between the crosslinks.
15. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8700 g/mol between the crosslinks.
16. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8600 g/mol between the crosslinks.
17. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8400 g/mol between the crosslinks.
18. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8300 g/mol between the crosslinks.
19. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8200 g/mol between the crosslinks.
20. A condom of claim 1 , wherein the intra-polyisoprene particle crosslinks and the inter-polyisoprene particle crosslinks are such that the molecular weight is less than about 8100 g/mol between the crosslinks.