Impact modified polycarbonate compositions
The invention relates to thermoplastic polycarbonate compositions which are impact-modified with ABS type polymers, said polycarbonate compositions being impact-modified with ABS type polymers are characterized by their excellent low temperature ductility, good processing properties expressed by relatively high melt volume rate (MVR) and good hydrolytic stability.
1. Resin composition comprising a homogenous blend of:
A) 5 to 99 wt.-parts of at least one aromatic polycarbonate,
B) 1 to 95 wt.-parts of at least one graft rubber copolymer which is produced by:
emulsion polymerization of styrene and acrylonitrile in the weight ratio 95:5 to 50:50, whereby styrene and/or acrylonitrile wholly or partially can be replaced by copolymerizable monomers, onto at least two rubber latices, comprising:
a butadiene rubber latex (B1) having a weight median particle diameter D 50 of 100 to 250 nm, and a gel content from 30 to 80% by weight, and
a butadiene rubber latex (B2) having a weight median particle diameter D 50 of more than 350 nm, and a gel content of less than 75% by weight,
C) optionally 0 to 50 wt.-parts of one or more (co)polymer of at least one monomer selected from the group consisting of vinyl aromatic monomers, vinyl cyanides and unsaturated carboxylic acids and derivatives thereof,
D) optionally 0 to 25 wt.-parts of conventional polymer additives, wherein
the weight median particle diameter D 50 of the mixture of the butadiene rubber latices (B1) and (B2) is larger than 350 nm and is less than 1000 nm, and the amount of the butadiene rubber latex polymer (B1) in the graft rubber copolymer B) is 1 to 49% by weight (B1) and the amount of the butadiene rubber latex polymer (B2) is 51 to 99% by weight, based on the total weight of the rubber latex polymers in the graft rubber copolymer B).
2. Resin composition according to claim 1 , wherein the rubber latices of graft rubber copolymer B) consist of butadiene rubber latex polymer (B1) and butadiene rubber latex polymer (B2).
3. Resin composition according to claim 1 , wherein the butadiene rubber latex polymer (B1) has a weight median particle diameter D 50 of 150 to 220 nm and/or has a gel content from 60 to 80% by weight.
4. Resin composition according to claim 1 , wherein the butadiene rubber latex polymer (B2) has a weight median particle diameter D 50 of 360 to 450 nm, and/or has a gel content of less than 70% by weight.
5. Resin composition according to claim 1 , wherein the graft rubber copolymer B) is produced by common grafting onto a mixture of the at least two rubber lattices, comprising said a butadiene rubber latex (B1) and (B2).
6. Resin composition according to claim 1 , wherein the graft rubber copolymer B) is produced by grafting of styrene and acrylonitrile onto the butadiene rubber lattices.
7. Resin composition according to claim 1 , wherein the graft rubber copolymer B) is produced by grafting of 30 to 50 parts by weight styrene and acrylonitrile onto 50 to 70 parts by weight of the butadiene rubber latices.
8. Resin composition according to claim 1 , wherein the aromatic polycarbonate is a polycarbonate based on bisphenol A and phosgene.
9. Resin composition according to claim 1 , which comprises at least one said (co)polymer C).
10. Resin composition according to claim 1 , which comprises at least one said (co)polymer C) which is a copolymer of styrene and acrylonitrile.
11. Resin composition according to claim 1 , wherein the conventional polymer additive (component D) is selected from the group of stabilizers, flame retarding agents, flameproofing synergists, antidripping agents, lubricants and mold release agents, nucleating agents, antistatics, fillers and reinforcing substances, dyestuffs and pigments.
12. Resin composition according to claim 1 , comprises comprising
A) 30 to 80 wt.-% of said at least one aromatic polycarbonate,
B) 5 to 30 wt.-% of said at least one graft rubber copolymer, and
C) 10 to 40 wt.-% of said one or more (co)polymer, and
optionally 0 to 25 wt.-% of said conventional polymer additives D), the weight-percentages being based on the total weight of the resin composition.
13. Process for the manufacture of the resin composition according to claim 1 , comprising the steps of:
a) preparing at least one graft rubber copolymer B) by emulsion polymerization of styrene and acrylonitrile in the weight ratio 95:5 to 50:50, whereby styrene and/or acrylonitrile wholly or partially can be replaced by copolymerizable monomers, onto at least two rubber latices, comprising: a butadiene rubber latex (B1) having a weight median particle diameter D 50 of 100 to 250 nm, and a gel content from 30 to 80% by weight, and a butadiene rubber latex (B2) having a weight median particle diameter D 50 of more than 350 nm, and a gel content of less than 75% by weight, and
b) admixing the graft rubber copolymer B) obtained in step a) with at least one aromatic polycarbonate A) and optionally 0 to 50 wt.-parts of one or more (co)polymer of at least one monomer selected from the group consisting of vinyl aromatic monomers, vinyl cyanides and unsaturated carboxylic acids and derivatives thereof, optionally 0 to 25 wt.-parts of conventional polymer additives.
14. A method for the manufacture of shaped or molded articles, comprising the steps of:
(i) providing a molding composition comprising the resin composition according to claim 1 , and
(ii) shaping or molding said molding composition.
15. Shaped or molded articles, comprising the resin composition according to claim 1 .
16. Resin composition according to claim 2 , wherein the butadiene rubber latex polymer (B1) has a weight median particle diameter D 50 of 150 to 220 nm and/or has a gel content from 60 to 80% by weight.
17. Resin composition according to claim 16 , wherein the butadiene rubber latex polymer (B2) has a weight median particle diameter D 50 of 360 to 450 nm, and/or has a gel content of less than 70% by weight.
18. Resin composition according to claim 3 , wherein the butadiene rubber latex polymer (B2) has a weight median particle diameter D 50 of 360 to 450 nm, and/or has a gel content of less than 70% by weight.
19. Resin composition according to claim 2 , wherein the butadiene rubber latex polymer (B2) has a weight median particle diameter D 50 of 360 to 450 nm, and/or has a gel content of less than 70% by weight.
20. Resin composition according to claim 17 , wherein the graft rubber copolymer B) is obtained by common grafting onto a mixture of the at least two rubber lattices, comprising said a butadiene rubber latex (B1) and (B2).
21. The method according to claim 14 , wherein the shaping or molding of the molding composition in step (ii) is performed by an injection molding, extrusion or blow molding process or by thermoforming of previously produced sheets or films.
22. Resin composition according to claim 6 , wherein the graft rubber copolymer B) is produced by grafting of 60 to 90% by weight styrene and 10 to 40% by weight acrylonitrile onto the butadiene rubber latices, the weight percentages relating to the total weight of styrene and acrylonitrile.