Anti-glare surface treatment method and articles thereof
A glass article including: at least one anti-glare surface having haze, distinctness-of-image, surface roughness, and uniformity properties, as defined herein. A method of making the glass article includes, for example, depositing sacrificial particles on a surface of the article; and contacting the resulting particulated surface with an etchant. A display system that incorporates the glass article, as defined herein, is also disclosed.
1. A method of making an article having an anti-glare surface, comprising:
depositing glass particles to adhere the particles on at least one glass surface of the article, wherein depositing glass particles on at least one glass surface of the article comprises:
forming a concentrated liquid suspension of the glass particles,
diluting the concentrated suspension with a liquid diluent, and
contacting the at least one glass surface and the diluted suspension; and
contacting the at least one glass surface of the article having the deposited and adhered glass particles and an etchant to form the anti-glare surface, and the etchant comprises at least one acid, wherein the anti-glare surface has a haze of from about 0.1 to about 30, a distinctness-of-image (DOI 20°) of from about 25 to about 85, and a surface roughness (Ra) of from about 50 to about 500 nm.
2. The method of claim 1 wherein the surface glass and the glass particles are independently comprised of at least one of a soda lime silicate glass, an alkaline earth aluminosilicate glass, an alkali aluminosilicate glass, an alkali borosilicate glass, a boroaluminosilicate glass, or a combination thereof, and the at least one etchant comprises at least one acid selected from HF, H 2 SO 4 , or a combination thereof.
3. The method of claim 1 wherein contacting the at least one surface of the article having the deposited glass particles and an etchant comprises exposing the surface having the deposited particles to the etchant for about 1 second to about 30 minutes.
4. The method of claim 1 wherein the deposited glass particles have a D 50 diameter of from about 1 to about 30 micrometers.
5. The method of claim 1 further comprising washing the resulting anti-glare surface, chemically strengthening the anti-glare surface, or a combination thereof.
6. The method of claim 1 further comprising, prior to etching, contacting at least another surface of the article with a removable, etch-resistant protective layer.
7. A method of creating an anti-glare glass surface, comprising:
contacting a glass surface with a liquid diluted suspension of glass particles to produce a particulated glass surface; and
contacting the resulting particulated glass surface and an etchant to form the anti-glare surface.