Silver-coated spherical resin, method for producing same, anisotropically conductive adhesive containing silver-coated spherical resin, anisotropically conductive film containing silver-coated spherical resin, and conductive spacer containing silver-coated spherical resin
This silver-coated spherical resin includes: a spherical resin; and silver coated on a surface of the spherical resin, wherein an amount of the silver is in a range of 2 to 80 parts by mass with respect to 100 parts by mass of the silver-coated spherical resin, and a crystallite diameter of the silver measured by X-ray diffractometry is in a range of 18 to 24 nm. This method for producing a silver-coated spherical resin includes: a process of subjecting a spherical resin to a pretreatment using an aqueous solution of a tin compound; and a subsequent process of subjecting the spherical resin to an electroless silver plating using a reducing agent, wherein, during the pretreatment, a temperature of the aqueous solution of the tin compound is set to be in a range of 20 to 45° C.
1. A silver-coated spherical resin comprising:
a spherical resin consisting of an acryl-based resin;
a tin adsorption layer provided on a surface of the spherical resin; and
silver coated on a surface of the tin adsorption layer,
wherein an amount of the silver is in a range of 2 to 80 parts by mass with respect to 100 parts by mass of the silver-coated spherical resin, and
a crystallite diameter of the silver measured by X-ray diffractometry is in a range of 18 to 24 nm.
2. The silver-coated spherical resin according to claim 1 ,
wherein an average particle diameter of the spherical resin is in a range of 0.5 to 40 pim, and a variation coefficient of particle diameters thereof is in a range of 5.0% or less.
3. The silver-coated spherical resin according to claim 1 ,
wherein, when a single particle of the silver-coated spherical resin is compressed by 20% of the particle diameter thereof in one direction, a resistance in a compression direction thereof is in a range of 100Ω or lower.
4. The silver-coated spherical resin according to claim 1 ,
wherein, when a single particle of the silver-coated spherical resin is compressed by 50% of the particle diameter thereof in one direction, a resistance in a compression direction thereof is in a range of 10Ω or lower.
5. A method for producing a silver-coated spherical resin comprising:
a process of subjecting a spherical resin to a pretreatment using an aqueous solution of a tin compound; and
a subsequent process of subjecting the spherical resin to an electroless silver
plating using a reducing agent,
wherein, during the pretreatment, a temperature of the aqueous solution of the tin compound is set to be in a range of 30 to 45° C.
6. The method for producing a silver-coated spherical resin according to claim 5 ,
wherein the reducing agent comprises formaldehyde.
7. The method for producing a silver-coated spherical resin according to claim 6 ,
wherein the reducing agent further comprises glucose.
8. An anisotropically conductive adhesive comprising:
the silver-coated spherical resin according to claim 1 .
9. An anisotropically conductive film comprising:
the silver-coated spherical resin according to claim 1 .
10. A conductive spacer comprising:
the silver-coated spherical resin according to claim 1 .