Multimetallic nanoparticle catalysts with enhanced electrooxidation
A new structure-control strategy to optimize nanoparticle catalysis is provided. The presence of Au in FePtAu facilitates FePt structure transformation from chemically disordered face centered cubic (fcc) structure to chemically ordered face centered tetragonal (fct) structure, and further promotes formic acid oxidation reaction (FAOR). The fct-FePtAu nanoparticles show high CO poisoning resistance, achieve mass activity as high as about 2810 mA/mg Pt, and retain greater than 90% activity after a 13 hour stability test.
1. A method of manufacturing FePtAu nanoparticle (NP) catalyst comprising:
co-reducing platinum acetylacetone (Pt(acac) 2 ) and chloroauric acid hydrate (HAuCl 4 .xH 2 O) by mixing each in a solvent in the presence of oleylamine and tetradecylphosphonic acid, and heating to form a solution;
adding iron pentacarbonyl (Fe(CO) 5 ) to the solution and further heating the solution, thereby thermally decomposing (Fe(CO) 5 ) and obtaining nanoparticies;
separating by precipitation and purifying the nanoparticles thereby obtaining as-synthesized nanoparticles; and,
annealing the as-synthesized nanoparticles at a high temperature, whereby surfactant materials on or coating the as-synthesized nanoparticles are removed, and the as-synthesized nanoparticles are converted by a high temperature transition from a structure that is chemically disordered face centered cubic, fcc-FePtAu, to a chemically ordered face centered tetragonal, fct-FePtAu, thereby obtaining the FePtAu NP catalyst.
2. The method according to claim 1 , wherein the as-synthesized nanoparticles are annealed at a temperature range of about 400-650° C. for about 1 hour.
3. The method according to claim 1 further comprising prior to annealing, depositing the as-synthesized nanoparticles on a solid support, wherein the solid support prevents aggregation/sintering of the nanoparticles during the high temperature annealing.
4. The method according to claim 3 wherein the solid support is Ketjen carbon.
5. The method according to claim 1 , wherein prior to obtaining nanoparticles the method further comprises selecting a molar ratio of components (Pt(acac) 2 ), (HAuCl 4 .xH 2 O) and (Fe(CO) 5 ).
6. A method of using trimetallic FePtAu nanoparticle (NP) catalyst for promoting a formic acid oxidation reaction (FAOR), the method comprising oxidizing formic acid (HCOOH) in an electrochemical cell in the presence of N 2 -saturated sulfuric acid (H 2 SO 4 ) and the NP catalyst.
7. The method according to claim 6 wherein the trimetallic FePtAu nanoparticle (NP) catalyst has a chemically ordered face-centered tetragonal (fct) structure, in which Fe and Pt atoms alternate in atomic layers along one direction and Au is enriched on the surface of the FePtAu NP.
8. The method according to claim 7 , wherein oxidizing HCOOH is essentially due to direct oxidation of HCOOH to CO 2 .
9. The method according to claim 7 , wherein the concentration of H 2 SO 4 is 0.1 to 1.0 molar (M).
10. The method according to claim 7 , wherein the concentration of HCOOH is 0.2 to 2.0 M.