Fiber-reinforced resin composition
A fiber-reinforced resin composition which is capable of providing a light-weight molded article that has a high mechanical strength. The fiber-reinforced resin composition contains (A) a thermoplastic resin and (B) resin-impregnated filament bundles containing rayon fibers. The rayon fibers of the component (B) have a fiber diameter of 5-30 μm and an X-ray orientation degree of 86% or more. The resin-impregnated filament bundles are obtained by: tying 2,000-30,000 rayon fibers of the component (B) lined up in the longitudinal direction together in a bundle; integrating the bundle of the rayon fibers by impregnating the bundle with the thermoplastic resin of the component (A) in a molten state; and then cutting the integrated bundle into pieces 3-30 mm long.
1. A fiber-reinforced resin composition comprising a resin-impregnated long fiber bundle including (A) a thermoplastic resin and (B) a rayon fiber, wherein
the rayon fiber of component (B) has a fiber diameter of 5 to 30 μm and an X-ray orientation degree of 90% or more, and
the resin-impregnated long fiber bundle is obtained by impregnating a bundle of 2,000 to 30,000 rayon fibers of component (B) in a state where the rayon fibers are arranged in the longitudinal direction, with the thermoplastic resin of the component (A) in a molten state to thereby form an integrated bundle, and then cutting the integrated bundle into a length of 3 to 30 mm.
2. The fiber-reinforced resin composition according to claim 1 , wherein the rayon fiber of component (B) has a tensile modulus of 10 GPa or more.
3. The fiber-reinforced resin composition according to claim 1 , wherein the rayon fiber of component (B) has a tensile modulus of 13 GPa or more.
4. The fiber-reinforced resin composition according to claim 1 , wherein the thermoplastic resin of component (A) is selected from a polyolefin resin and a polyamide resin.
5. The fiber-reinforced resin composition of claim 1 , wherein the thermoplastic resin of component (A) includes polypropylene and maleic acid-modified polypropylene and/or maleic anhydride-modified polypropylene and
an acid amount in component (A) is, on average, 0.005 to 0.5% by mass in terms of maleic anhydride.
6. The fiber-reinforced resin composition of claim 1 , wherein the thermoplastic resin of component (A) is selected from an aliphatic polyamide of polyamide 6, polyamide 69, polyamide 610, polyamide 612, polyamide 11 and polyamide 12.
7. A molded article obtained from the fiber-reinforced resin composition of claim 1 .
8. The molded article according to claim 7 , wherein a specific modulus of a 4 mm thick molded article is 4,000 MPa or more.
9. The molded article according to claim 7 , wherein a specific modulus of a 4 mm thick molded article is 4,500 MPa or more.