Method for pretreating lignocellulosic biomass
View Patent ↗The present invention relates to a method for pretreating lignocellulosic biomass containing alkali and/or alkaline earth metal (AAEM). The method comprises providing a lignocellulosic biomass containing AAEM; determining the amount of the AAEM present in the lignocellulosic biomass; identifying, based on said determining, the amount of a mineral acid sufficient to completely convert the AAEM in the lignocellulosic biomass to thermally-stable, catalytically-inert salts; and treating the lignocellulosic biomass with the identified amount of the mineral acid, wherein the treated lignocellulosic biomass contains thermally-stable, catalytically inert AAEM salts.
1. A method for pretreating lignocellulosic biomass containing alkali and/or alkaline earth metal (AAEM) comprising:
providing a lignocellulosic biomass containing AAEM;
determining the amount of the AAEM present in the lignocellulosic biomass;
identifying, based on said determining, the amount of a mineral acid sufficient to titrate the AAEM present in the lignocellulosic biomass and to completely convert the mineral acid and the AAEM in the lignocellulosic biomass to thermally-stable, catalytically-inert salts without requiring residual acid disposal; and
treating the lignocellulosic biomass with the identified amount of the mineral acid to produce a treated lignocellulosic biomass containing thermally-stable, catalytically inert AAEM salts, wherein said method does not remove the catalytically-inert AAEM salts from the lignocellulosic biomass.
2. The method of claim 1 further comprising:
drying the treated lignocellulosic biomass.
3. The method of claim 1 further comprising:
pyrolyzing the treated lignocellulosic biomass to obtain a bio-oil product.
4. The method of claim 3 , wherein the obtained bio-oil product comprises anhydrosugars, monosaccharides, and oligosaccharides.
5. The method of claim 3 , wherein the sugar yield in the bio-oil product is increased by 2-9 fold compared to a bio-oil product produced from the provided lignocellulosic biomass which is not subjected to said treating.
6. The method of claim 3 , wherein the bio-oil product has a sugar yield of 18-25 wt % compared to a bio-oil product produced from the provided lignocellulosic biomass which is not subjected to said treating having a sugar yield of only 2-6 wt%.
7. The method of claim 3 , wherein the bio-oil product has a light oxygenated compound yield which is decreased by 8-15 wt % compared to a bio-oil product produced from the provided lignocellulosic biomass which is not subjected to said treating.
8. The method of claim 3 , wherein said pyrolyzing is carried out at a temperature ranging from 300° C. to 500° C.
9. The method of claim 1 , wherein the lignocellulosic biomass is selected from the group consisting of softwood, hardwood, grasses, crop residues, and mixtures thereof.
10. The method of claim 1 , wherein the molar concentration of AAEM salts in the acid-treated lignocellulosic biomass ranges from 0.065 to 0.40 mmol per gram of biomass.
11. The method of claim 1 , wherein said treating is carried out with 0.04 to 0.50 mmol mineral acid per gram of biomass.
12. The method of claim 1 , wherein the mineral acid is sulfuric acid, phosphoric acid, or hydrochloric acid.
13. The method of claim 3 , wherein said pyrolyzing is carried out in a continuous flow reactor.
14. The method of claim 3 , wherein said pyrolyzing is carried out in an auger-type reactor.
15. The method of claim 14 , wherein said pyrolyzed bio-oil from the auger-type reactor product comprises 15-30 wt% sugar.