Adhesive composition with improved green strength
Adhesive composition comprising : at most 15% of a PolyPropylene (or PP) having a melting point between 30° C. and 100° C. ; from 30 to 60% of a cross-linkable polymer with silyl end groups comprising cross-linking groups bonded to the silicon atom, said cross-linkable polymer having a functionality of on average 3-12 cross-linking groups; a cross-linking catalyst for the polymer; a water scavenger; and a rheology controller. The composition is used for direct glazing of a windscreen on a metallic automotive frame.
1. Adhesive composition comprising:
a content of greater than 0 and less than 15% by weight of a PolyPropylene having a melting point between 30° C. and 100° C.;
from 30 to 60% by weight of a cross-linkable polymer with silyl end groups comprising cross-linking groups bonded to the silicon atom, the cross-linkable polymer having a functionality of on average 3-12 cross-linking groups;
a cross-linking catalyst for the cross-linkable polymer;
a water scavenger; and
a rheology controller.
2. The adhesive composition according to claim 1 , wherein the content of PP is from 2 to 10% by weight.
3. The adhesive composition according to claim 1 , wherein the silyl end group of the cross-linkable polymer has the following formula:
—Si(R 2 ) 3-a X a
wherein:
R 2 represents an alkyl group containing 1 to 20 carbon atoms, an aryl group containing 6 to 20 carbon atoms, an aralkyl group containing 7 to 20 carbon atoms or a triorganosiloxy group of the formula (R′) 3 SiO—, in which the three R′ groups are the same or different and each is a monovalent hydrocarbon group containing 1 to 20 carbon atoms, and when there are two or more R 2 groups, they may be the same or different;
X represents a hydroxyl group or a hydrolysable group and, when there are two or more X groups, they may be the same or different;
a represents 0, 1, 2 or 3.
4. The adhesive composition according to claim 1 , wherein the silyl end group of the cross-linkable polymer has the following formula:
—[Si(R 1 2-b )(X b )O] m Si(R 2 ) 3-a X a
wherein :
R 1 and R 2 are the same or different and each represents an alkyl group containing 1 to 20 carbon atoms, an aryl group containing 6 to 20 carbon atoms, an aralkyl group containing 7 to 20 carbon atoms or a triorganosiloxy group of the formula (R′) 3 SiO—, in which the three R′ groups are the same or different and each is a monovalent hydrocarbon group containing 1 to 20 carbon atoms, and when there are two or more R 1 or R 2 groups, they may be the same or different;
X represents a hydroxyl group or a hydrolysable group and, when there are two or more X groups, they may be the same or different;
a represents 0, 1, 2 or 3;
b represents 0, 1, or 2 and the value of b in two or more recurring units may be the same or different;
m represents an integer of 0 to 19;
with the condition that the relation a +Σb≧1 is satisfied.
5. The adhesive composition according to claim 4 , wherein the silyl end group of the cross-linkable polymer has the following formula:
-A-(CH 2 ) n —CHR 3 —CH 2 —[Si(R 1 2-b )(X b )O] m Si(R 2 ) 3-a X a
where:
n is zero or 1;
R 3 is a saturated or unsaturated alkyl group having 1-4 C atoms, a hydroxyl group, or a thiol group; and wherein the saturated or unsaturated alkyl group is optionally substituted by a hydroxyl or thiol group; and
A is an oxo, thio, carbamate or ureido linkage.
6. The adhesive composition according to claim 1 , wherein the cross-linkable polymer comprises a polyether polymer, a polyether-urethane polymer, a polyester polymer, a polyester-polyurethane polymer or mixtures thereof.
7. The adhesive composition according to claim 1 , wherein the cross-linkable polymer is a polyoxypropylene polymer having a silyl group at each end of its chain.
8. The adhesive composition according to claim 1 , wherein the water scavenger is an alkoxysilane present in an amount from about 1% to about 10% by weight.
9. The adhesive composition according to claim 1 , wherein the rheology controller is a polyamide wax present in a quantity of 1% to 5% by weight.
10. The adhesive composition according to claim 1 , wherein the content of PP is from 4 to 8% by weight.
11. A method for direct glazing of a windscreen on a metallic automotive frame, comprising:
(i) applying the composition defined in claim 1 on the windscreen and/or frame; and
(ii) securing the windscreen and the frame together,
wherein the composition is warmed to a temperature between 30° C. and 100° C. before it is applied on the windscreen and/or frame.
12. The method according to claim 11 wherein the composition is warmed to a temperature from 50° C. to 90° C.