Luminescent material
According to one embodiment, the luminescent material exhibits a luminescence peak in a wavelength ranging from 500 to 600 nm when excited with light having an emission peak in a wavelength ranging from 250 to 500 nm. The luminescent material has a composition represented by Formula 1 below: (M 1-x Ce x ) 2y Al z Si 10-z O u N w Formula 1 wherein M represents Sr and a part of Sr may be substituted by at least one selected from Ba, Ca, and Mg; x, y, z, u, and w satisfy following conditions: 0<x≦1, 0.8≦y≦1.1, 2≦z≦3.5, u≦1 1.8≦z−u, and 13≦u+w≦15.
1. A luminescent material which exhibits a luminescence peak in a wavelength ranging from 544 to 562 nm when excited with light having an emission peak in a wavelength ranging from 250 to 500 nm, the luminescent material having a composition represented by Formula 1 below:
(M 1-x Ce x ) 2y Al z Si 10-z O u N w Formula 1
wherein M represents Sr and a part of Sr may be substituted by at least one selected from Ba, Ca, and Mg; x, y, z, u, and w satisfy following conditions:
0<x≦1, 0.8≦y≦1.1, 2≦z≦3.5, u≦1,
1.8≦z−u, and 13≦u+w≦15,
and wherein a crystal of the luminescent material has an orthorhombic system and belongs to a space group Pna2 1 .
2. The luminescent material according to claim 1 , wherein the luminescent material has at least ten peaks at diffraction angles (2θ) of 15.05-15.15, 23.03-23.13, 24.87-24.97, 25.7-25.8, 25.97-26.07, 29.33-29.43, 30.92-31.02, 31.65-31.75, 31.88-31.98, 33.02-33.12, 33.59-33.69, 34.35-34.45, 35.2-35.3, 36.02-36.12, 36.55-36.65, 37.3-37.4, and 56.5-56.6 in X-ray diffraction by the Bragg-Brendano method using Cu—Kα line.
3. The luminescent material according to claim 1 , wherein x is from 0.001 to 0.5.
4. The luminescent material according to claim 1 , wherein y is from 0.85 to 1.06.
5. The luminescent material according to claim 1 , wherein z is from 2.5 to 3.3.
6. The luminescent material according to claim 1 , wherein u is from 0.001 to 0.8.
7. The luminescent material according to claim 1 , wherein z−u is 2 or more.
8. The luminescent material according to claim 1 , wherein u+w is from 13.2 to 14.2.
9. The luminescent material according to claim 1 , wherein 15 at % or less of Ce is replaced with another element.
10. The luminescent material according to claim 9 , wherein another element is selected from the group consisting of Tb, Eu, and Mn.
11. A light-emitting device comprising:
a light-emitting element which emits light having an emission peak in a wavelength ranging from 250 to 500 nm; and
a luminous layer comprising a luminescent material which emits yellow light by receiving light from the light-emitting element, the luminescent material which emits yellow light comprising the luminescent material of to claim 1 .
12. The light-emitting device according to claim 11 , further comprising:
a heat-dissipative insulation substrate on which the light-emitting element is placed,
wherein the luminous layer is dome-shaped.
13. The light-emitting device according to claim 12 , further comprising:
an inside transparent resin layer placed inside the luminous layer, and
an outside transparent resin layer placed outside the luminous layer.
14. The light-emitting device according to claim 11 , wherein the luminous layer further comprises at least one selected from the group consisting of a luminescent material which emits green light by excitation with blue light and a luminescent material which emits red light by excitation with blue light.
15. The light-emitting device according to claim 11 , wherein the light-emitting element emits ultraviolet ray having a peak in a wavelength ranging from 250 to 400 nm and the luminous layer further comprises a luminescent material which emits blue light by excitation with ultraviolet ray.
16. The light-emitting device according to claim 15 , wherein the fluorescent-emitting layer further comprises at least one selected from the group consisting of a luminescent material which emits red light by excitation with ultraviolet ray and a luminescent material which emits green light by excitation with ultraviolet ray.
17. A method for manufacturing a luminescent material of claim 1 , comprising:
mixing an M raw material selected from nitrides and carbides of M, an Al raw material selected from nitrides, oxides, and carbides of Al, an Si raw material selected from nitrides, oxides, and carbides of Si, and a Ce raw material selected from oxides, nitrides, and carbonates of Ce to obtain a mixture; and
heating the mixture under 5 atmospheres or more at 1500 to 2000° C.
18. The method according to claim 17 , wherein the mixture is heated in a nitrogen atmosphere.
19. The luminescent material according to claim 1 , wherein the luminescent material exhibits a luminescence peak in a wavelength ranging from 544 to 555 nm when excited with light having an emission peak in a wavelength ranging from 250 to 500 nm.