Electrode material for aluminum electrolytic capacitor and process for producing the electrode material
The present invention provides an electrode material for use in an aluminum electrolytic capacitor that does not necessitate an etching treatment. Specifically, the present invention provides an electrode material for use in an aluminum electrolytic capacitor, the electrode material comprising a sintered body of at least one of aluminum and an aluminum alloy.
1. A method for producing a medium- to high-voltage aluminum electrolytic capacitor including an electrode and an electrolyte,
wherein an electrode material for the electrode is produced by a method comprising the steps of:
Step (1): forming a film made from a composition comprising a powder of at least one of aluminum and an aluminum alloy on a substrate; and
Step (2): sintering the film at a temperature not lower than 560° C. and not higher than 660° C. so that particles of the powder of at least one of aluminum and an aluminum alloy maintain a space between each particle;
the method being free from an etching treatment,
the method comprising a degreasing treatment after Step (1) and prior to Step (2), at a temperature within a range of not lower than 100° C. to not higher than 600° C. and the temperature is maintained for not less than 5 hours, and
a porosity of the resulting sintered body is determined by a target electrostatic capacity, and is not less than 10%, and the powder having an average particle diameter of not less than 1 μm and not more than 80 μm,
wherein the porosity is controlled by controlling a particle diameter of the powder of at least one of aluminum and an aluminum alloy.
2. The production method according to claim 1 , wherein the composition comprises at least one member selected from the group consisting of resin binders and solvents.
3. The method according to claim 1 , further comprising the step of forming a capacitor element by laminating an anode foil using the electrode material and a cathode foil with a separator therebetween, and winding the resulting laminate.
4. A method for producing a medium- to high-voltage aluminum electrolytic capacitor including an electrode and an electrolyte,
wherein the electrode is produced by a method comprising the steps of:
Step (1): forming a film made from a pasty composition comprising a powder of at least one of aluminum and an aluminum alloy on a substrate; and
Step (2): sintering the film at a temperature not lower than 560° C. and not higher than 660° C. so that particles of the powder of at least one of aluminum and an aluminum alloy maintain a space between each particle;
the method being free from an etching treatment,
the method comprising a degreasing treatment after Step (1) and prior to Step (2), at a temperature within a range of not lower than 100° C. to not higher than 600° C. and the temperature is maintained for not less than 5 hours, and
a porosity of the resulting sintered body is determined by a target electrostatic capacity, and is not less than 10%, and the powder having an average particle diameter of not less than 1 μm and not more than 80 μm,
wherein the porosity is controlled by controlling a particle diameter of the powder of at least one of aluminum and an aluminum alloy.
5. The production method according to claim 4 , which further comprises step (3): anodizing the sintered film.
6. The method according to claim 4 , further comprising the step of forming a capacitor element by laminating an anode foil using the electrode material and a cathode foil with a separator therebetween, and winding the resulting laminate.