View Patent ↗The present invention relates to a process for manufacturing a segmented optical structure ( 100 ), comprising at least the steps consisting in: a) providing a substrate ( 1 ) having microwalls ( 2 ) on one of the faces ( 3 ) of said substrate, which microwalls form, when the substrate ( 1 ) is observed along an axis (X) perpendicular to said face, a plurality of concentric recesses ( 5 ); b) depositing at least one material ( 10; 10 a; 10 b; 10 c ) in at least one recess ( 5 ); c) bringing at least one part of the upper surface ( 11 ) of the material ( 10; 10 a; 10 b; 10 c ) deposited in step b) into contact with at least one liquid medium ( 30 ) which is capable of dissolving said material ( 10; 10 a; 10 b; 10 c ) and is substantially inert with respect to the microwalls ( 2 ) and to the substrate ( 1 ); and d) imposing a centrifugal force on the liquid medium ( 30 ) deposited in step c) so as to modify the distribution thereof on the upper surface ( 11 ) of the material ( 10; 10 a; 10 b; 10 c ) deposited during step b), the amount of liquid medium ( 30 ) used during step c) enabling the material deposited during step b) to be partially dissolved.
1. A process for manufacturing a segmented optical structure comprising at least steps consisting in:
a) providing a substrate equipped, on one of its faces, with microwalls forming, when the substrate is observed along axis (X) perpendicular to said face, a plurality of concentric voids;
b) depositing at least one material in at least one void to produce a deposit having top surface;
c) bringing at least one part of the top surface of the material deposited in step b) into contact with an amount of at least one liquid medium that dissolves said material and that is inert with respect to the microwalls and substrate; and
d) applying a centrifugal force to the liquid medium deposited in step c) so as to modify its distribution over the top surface of the material deposited in step b);
wherein the amount of liquid medium used in step c) enables partial dissolution of the deposit produced in step b).
2. The process of claim 1 , wherein step d) is initiated during or consecutively to step c).
3. The process of claim 1 , wherein the liquid medium is discontinuously and controllably dispensed on at least one part of the top surface of the deposit produced in step b).
4. The process of claim 1 , wherein the liquid medium is applied to at least 25% of the top surface of the deposit produced in step b).
5. The process of claim 1 , wherein step c), step d), or steps c) and d) takes place in a chamber in which the temperature is between 3° C. and 50° C.
6. The process of claim 1 , wherein step c), step d), or steps c) and d) takes place in a chamber in which the relative humidity is between 10% and 70%.
7. The process of claim 1 , wherein the material in step b) is deposited in substantially all the voids.
8. The process of claim 1 , wherein the deposit produced in step b) has a constant height.
9. The process of claim 1 , wherein the deposit produced in step b) has a varying height.
10. The process of claim 1 , wherein a plurality of different materials are deposited in step b).
11. The process of claim 1 , wherein a plurality of different liquid mediums are dispensed in step c).
12. The process of claim 1 , wherein the microwalls comprise:
an organic polymer;
a hybrid sol-gel material; or
a mixture thereof.
13. The process of claim 12 , wherein the organic polymer is a photoresist in form of a liquid or in form of a dry film.
14. The process of claim 12 , wherein the liquid medium comprises:
an acid;
an alcohol; and
a photoresist developer.
15. The process of claim 14 , wherein the acid is hydrofluoric acid and the alcohol is isopropyl alcohol, ethanol, or a mixture thereof.
16. The process of claim 1 , wherein the amount of liquid medium introduced into at least one void is adjustable such that the liquid medium covers all of the top surface of the deposit produced in said void.
17. The process of claim 1 , wherein the material deposited in step b) is a hybrid sol-gel material.
18. The process of claim 1 , wherein the segmented optical structure obtained is a lenticular structure.
19. The process of claim 18 , wherein the lenticular structure is a Fresnel lens.
20. The process of claim 18 , wherein the microwalls bound Fresnel zones of the Fresnel lens.