Dielectric ceramic composition, electronic element, and composite electric element
In order to provide a dielectric ceramic composition capable of sintering at a low temperature, implementing a low relative dielectric constant, providing other excellent properties (such as a relative density and an insulation resistance), performing co-firing of different materials, and suppressing dispersion of Ag in the sintered body when the internal electrode is formed, the dielectric ceramic composition includes a main ingredient containing SiO 2 —K 2 O—B 2 O 3 -based glass of 40 to 65 weight %, quartz of 35 to 50 weight %, and amorphous silica of remaining weight %; and a subsidiary ingredient containing alumina of 1.5 to 4 weight %, K 2 O-MO—SiO 2 —B 2 O 3 -based glass (where “MO” denotes at least any one selected from a group consisting of CaO and SrO) of 5 to 20 weight % relative to the main ingredient of 100 weight %.
1. A dielectric ceramic composition comprising:
a main ingredient containing SiO 2 —K 2 O—B 2 O 3 -based glass of 40 to 65 weight % of the main ingredient, quartz of 35 to 50 weight % of the main ingredient, and amorphous silica of remaining weight % of the main ingredient; and
a subsidiary ingredient containing alumina and K 2 O-MO—SiO 2 —B 2 O 3 -based glass, M being selected from the group consisting of Ca and Sr,
wherein the weight % ratio of alumina to the main ingredient is from 1.5:100 to 4:100,
wherein the weight % ratio of K 2 O-MO—SiO 2 —B 2 O 3 -based glass to the main ingredient is from 5:100 to 20:100, and
wherein the K 2 O-MO—SiO 2 —B 2 O 3 -based glass has a linear expansion coefficient of 105×10 −7 /° C. to 125×10 −7 /° C.
2. The dielectric ceramic composition according to claim 1 , wherein the SiO 2 —K 2 O—B 2 O 3 -based glass has a glass transition point of 480 to 520° C.
3. The dielectric ceramic composition according to claim 1 , wherein the K 2 O-MO—SiO 2 —B 2 O 3 -based glass has a softening point of 580 to 680° C.
4. An electronic element comprising a nonmagnetic layer, wherein the nonmagnetic layer has the dielectric ceramic composition according to claim 1 .
5. A multilayer composite electronic element comprising:
a filter portion having a coil conductor and a nonmagnetic layer; and
an exterior portion including the magnetic layer,
wherein the coil conductor contains Ag as a conductive material, and
the nonmagnetic layer has the dielectric ceramic composition according to claim 1 .
6. The multilayer composite electronic element according to claim 5 , wherein the multilayer composite electronic element is a multilayer common mode filter.
7. The multilayer composite electronic element according to claim 6 , further comprising an ESD conductor layer having an electrostatic discharge protection functionality.