Method for manufacturing porous glass, and method for manufacturing optical element
A method for manufacturing a porous glass includes: forming a phase-separated glass by heating at a temperature in a range of 300 to 500 degrees Celsius for 3 to 50 hours for phase separation of a glass body in which the concentration of SiO 2 is 50 to 70 percent by weight, the concentration of B 2 O 3 is 15 to 40 percent by weight, the concentration of Li 2 O is 1.0 to 8.0 percent by weight, the concentration of Na 2 O is 2.0 to 8.0 percent by weight, the concentration of K 2 O is 0.3 to 5.0 percent by weight, the total concentration of Li 2 O, Na 2 O, and K 2 O is 3.5 to 15 percent by weight, and the ratio of the concentration of K 2 O to the total concentration of Li 2 O, Na 2 O, and K 2 O is 0.10 to 0.30; and forming a porous glass by etching the phase-separated glass.
1. A method for manufacturing a porous glass comprising the steps of:
forming a phase-separated glass by heating at a temperature in a range of 300 to 500 degrees Celsius for 3 to 50 hours for phase separation of a glass body in which the concentration of SiO 2 is in a range of 50 to 70 percent by weight, the concentration of B 2 O 3 is in a range of 15 to 40 percent by weight, the concentration of Li 2 O is in a range of 1.0 to 8.0 percent by weight, the concentration of Na 2 O is in a range of 2.0 to 8.0 percent by weight, the concentration of K 2 O is in a range of 0.3 to 5.0 percent by weight, the total concentration of Li 2 O, Na 2 O, and K 2 O is in a range of 3.5 to 15 percent by weight, and the ratio of the concentration of K 2 O to the total concentration of Li 2 O, Na 2 O, and K 2 O is in a range of 0.10 to 0.30; and
forming a porous glass by etching the phase-separated glass.
2. The method for manufacturing a porous glass according to claim 1 ,
wherein in the glass body, the concentration of SiO 2 is in a range of 50 to 70 percent by weight, the concentration of B 2 O 3 is in a range of 20 to 35 percent by weight, the concentration of Li 2 O is in a range of 1.5 to 5.0 percent by weight, the concentration of Na 2 O is in a range of 2.0 to 6.0 percent by weight, the concentration of K 2 O is in a range of 0.8 to 4.0 percent by weight, and the total concentration of Li 2 O, Na 2 O, and K 2 O is in a range of 4.3 to 15 percent by weight.
3. The method for manufacturing a porous glass according to claim 1 ,
wherein in the glass body, the concentration of SiO 2 is in a range of 55 to 70 percent by weight, the concentration of B 2 O 3 is in a range of 25 to 35 percent by weight, the concentration of Li 2 O is in a range of 1.5 to 3.0 percent by weight, the concentration of Na 2 O is in a range of 2.5 to 5.5 percent by weight, the concentration of K 2 O is in a range of 0.8 to 3.0 percent by weight, and the total concentration of Li 2 O, Na 2 O, and K 2 O is in a range of 4.8 to 11 percent by weight.
4. A method for manufacturing an optical element having a porous glass,
wherein a step of forming the porous glass is performed by the method for manufacturing a porous glass according to claim 1 .
5. The method for manufacturing a porous glass according to claim 1 ,
wherein only SiO 2 , B 2 O 3 , Li 2 O, Na 2 O, and K 2 O are included in the glass body.