Highly absorbent composite and method of making the same

1. A method of making an absorbent sheet comprising the steps of:

preparing a three component dispersion slurry by adding and dispersing a short-cut staple fiber component and absorbent polymer particles in a dispersion liquid where hydratable fine fibers in the form of microfibril are dispersed in a dispersion medium, the short-cut staple fiber component having longer fiber length than average diameter of the absorbent polymer particles;

forming a slurry layer by spreading said three component dispersion slurry on at least either surface of a supporting sheet; and

removing said dispersion medium from said slurry layer and then drying,

wherein the ratio (P/Q) of weight (P) of said hydratable fine fibers in the form of microfibril to weight (Q) of said short-cut staple fiber component is in the range of from 1/5 to 5/1.

2. The method of claim 1 , wherein said short-cut staple fiber component is thermally fusible fibers, and which further comprises the step of heating and melting said staple fiber component at the melting or higher temperatures, in or after said step of removing the dispersion medium.

3. A method of making an absorbent sheet comprising the steps of:

preparing a two component dispersion liquid by dispersing hydratable fine fibers in the form of microfibril and absorbent polymer particles in a dispersion medium;

forming a first slurry layer by spreading said two component dispersion liquid on at least either surface of a supporting sheet;

forming a second slurry layer covering said first slurry layer by feeding a dispersion liquid where a short-cut staple fiber component is dispersed in a dispersion medium from the top of said first slurry layer, the short-cut staple fiber component having longer fiber length than average diameter of the absorbent polymer particles; and

removing said dispersion mediums from said first and second slurry layers, and then drying,

wherein the ratio (P/Q) of weight (P) of said hydratable fine fibers in the form of microfibril to weight (Q) of said short-cut staple fiber component is in the range of from 1/5 to 5/1.

4. A method of making an absorbent sheet comprising a supporting sheet, a first layer comprising two components of hydratable fine fibers in the form of microfibril and a short-cut staple fiber component, and a second layer comprising three components of absorbent polymer particles, hydratable fine fibers in the form of microfibril and a short-cut staple fiber component, said first and second layers being laid on at least one surface of said supporting sheet in a desired pattern, the short-cut staple fiber component having longer fiber length than average diameter of the absorbent polymer particles, comprising the steps of:

forming a slurry layer by spreading a slurry where hydratable fine fibers in the form of microfibril and short-cut staple fiber component are dispersed in a dispersion medium so that said absorbent polymer particles on the supporting sheet are covered; and

removing said dispersion medium from said slurry layer containing absorbent polymer particles and then drying,

wherein the ratio (P/Q) of weight (P) of said hydratable fine fibers in the form of microfibril to weight (Q) of said short-cut staple fiber component is in the range of from 1/5 to 5/1.

5. A method of making an absorbent sheet comprising the steps of:

preparing a dispersion liquid in the form of a slurry by dispersing absorbent polymer particles into a dispersion medium consisting of a water soluble polyvalent alcohol or a mixture of said alcohol with water;

storing said dispersion liquid;

forming said dispersion liquid into a sheet;

removing said dispersion medium from said sheet; and

drying said sheet to foam an absorbent body;

wherein the viscosity of said dispersion liquid slurry is lowered by heating said dispersion liquid in succession in a process from a transfer of said dispersion liquid to said forming step up to said removing step, and said polyvalent alcohol is selected from a group consisting of ethylene glycol, propylene glycol, diethylene glycol, triethylene glycol, low molecular weight polyethylene glycol and glycerin.

6. The method of claim 5 , wherein the viscosity is lowered by heating and adding an amount of water in the process leading up to the removing step.

7. The method of claim 5 , wherein said dispersion medium is a mixture of a polyvalent alcohol and water, the ratio of the polyvalent alcohol to water being 9/1 to 5/5.

8. The method of claim 5 , wherein the concentration of water to said polyvalent alcohol in said dispersion medium is increased in succession in said preparation step, said forming step and said removing step.

9. The method of claim 5 , wherein said dispersion liquid contains hydratable fine fibers in the form of microfibril finer than the average particle diameter of the absorbent polymer particles coexistent with said absorbent polymer particles to make a co-dispersion system.

10. The method of claim 9 , wherein said dispersion liquid in a liquid feeding step during said forming step is kept at a temperature of 30 C. or higher and 20 C. higher than the temperature in said storage step.

11. The method of claim 10 , wherein heating in said liquid feeding step is done by directly blowing saturated steam so that the polyvalent alcohol/water ratio is adjusted by the effect of heating and water addition to said dispersion liquid during said liquid feeding.

12. The method of claim 5 , wherein said dispersion liquid contains a short-cut staple fiber component having a length longer than the average particle diameter of said absorbent polymer particles and being fibrous material of 10 mm or shorter in fiber length and 3 denier or less in diameter.

13. The method of claim 5 , wherein said dispersion liquid contains a combination of hydratable fine fibers in the form of microfibril shorter and finer than the average particle diameter of said absorbent polymer particles and a short-cut staple fiber component having a fiber length longer than the average particle diameter of said absorbent polymer particles and of 10 mm or shorter in length and 3 denier or less in diameter.

14. The method of claim 5 , wherein the formed sheet obtained in said forming step is transferred to a steam treatment apparatus where heating of said formed sheet and water displacement are carried out whereby liquid removal is facilitated.