Polymers with improved ESCR for blow molding applications
Disclosed herein are ethylene-based polymers having a higher molecular weight component and a lower molecular weight component, and characterized by a density greater than 0.945 g/cm 3 , a melt index less than 1.5 g/10 min, and a ratio of high load melt index to melt index ranging from 40 to 175. These polymers have the processability of chromium-based resins, but with improved stiffness and stress crack resistance, and can be used in blow molding and other end-use applications.
1. An ethylene polymer comprising a higher molecular weight component and a lower molecular weight component, wherein the ethylene polymer has a density of greater than or equal to about 0.95 g/cm 3 , a melt index (MI) in a range from about 0.05 to about 1.5 g/10 min, a ratio of high load melt index to melt index (HLMI/MI) in a range from about 40 to about 175, a bimodal molecular weight distribution, less than about 0.008 long chain branches per 1000 total carbon atoms, a non-conventional comonomer distribution, and a slope of a plot of the viscosity (Pa-sec) versus shear rate (sec −1 ) at 190° C. of the ethylene polymer at 100 sec −1 in a range from about 0.42 to about 0.65.
2. The polymer of claim 1 , wherein the ethylene polymer has:
a density in a range from about 0.95 to about 0.965 g/cm 3 ;
a HLMI in a range from about 15 to about 100 g/10 min;
an ESCR (100% igepal) of at least 1000 hours; and
an ESCR (10% igepal) of at least 200 hours.
3. The polymer of claim 1 , wherein the ethylene polymer has:
a ratio of Mw/Mn in a range from about 6 to about 18;
a ratio of Mz/Mw in a range from about 6 to about 10;
a Mw in a range from about 150,000 to about 375,000 g/mol;
a Mn in a range from about 12,000 to about 35,000 g/mol; or
a Mz in a range from about 1,000,000 to about 3,000,000 g/mol; or
any combination thereof.
4. The polymer of claim 1 , wherein the ethylene polymer has:
a melt index in a range from about 0.1 to about 1 g/10 min;
a ratio of HLMI/MI in a range from about 60 to about 160; and
a density in a range from about 0.955 to about 0.965 g/cm 3 .
5. The polymer of claim 4 , wherein the ethylene polymer is an ethylene/α-olefin copolymer.
6. The polymer of claim 1 , wherein the ethylene polymer has:
a CY-a parameter at 190° C. in a range from about 0.02 to about 0.3; and
the slope of the plot of the viscosity (Pa-sec) versus shear rate (sec −1 ) at 190° C. of the ethylene polymer at 100 sec −1 in a range from about 0.44 to about 0.5.
7. The polymer of claim 1 , wherein the ethylene polymer is produced by a process comprising melt processing a mixture of a base resin and a peroxide compound in a twin screw extrusion system at a temperature in a range from about 120 to about 300° C. to generate peroxide groups at about 10-400 ppm of peroxide groups based on the weight of the base resin.
8. The polymer of claim 1 , wherein the ethylene polymer is an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, or an ethylene/1-octene copolymer.
9. An article comprising the ethylene polymer of claim 1 .
10. A blow molded article comprising the ethylene polymer of claim 1 .
11. An ethylene polymer comprising a higher molecular weight component and a lower molecular weight component, wherein the ethylene polymer has a density of greater than or equal to about 0.95 g/cm 3 , a melt index (MI) in a range from about 0.05 to about 1.5 g/10 min, a ratio of high load melt index to melt index (HLMI/MI) in a range from about 40 to about 175, a peak molecular weight (Mp) of the higher molecular weight component in a range from about 650,000 to about 1,100,000 g/mol, a Mp of the lower molecular weight component in a range from about 40,000 to about 80,000 g/mol, less than about 0.008 long chain branches per 1000 total carbon atoms, a non-conventional comonomer distribution, and a ratio of Mw/Mn in a range from about 5 to about 18.
12. The polymer of claim 11 , wherein the lower molecular weight component has:
a ratio of Mz/Mw in a range from about 1.5 to about 2.8;
a Mp in a range from about 45,000 to about 75,000 g/mol;
a Mw in a range from about 50,000 to about 80,000 g/mol; and
a Mn in a range from about 10,000 to about 30,000 g/mol.
13. The polymer of claim 11 , wherein the higher molecular weight component has:
a ratio of Mz/Mw in a range from about 1.5 to about 2.5;
a Mp in a range from about 700,000 to about 1,100,000 g/mol;
a Mw in a range from about 825,000 to about 1,500,000 g/mol; and
a Mn in a range from about 175,000 to about 700,000 g/mol.
14. The polymer of claim 11 , wherein the ethylene polymer has:
a density in a range from about 0.95 to about 0.965 g/cm 3 ;
a HLMI in a range from about 15 to about 100 g/10 min;
an ESCR (100% igepal) of at least 1000 hours; and
an ESCR (10% igepal) of at least 200 hours.
15. The polymer of claim 14 , wherein the ethylene polymer has:
a ratio of Mw/Mn in a range from about 6 to about 16; and
less than or equal to about 22 wt % of the higher molecular weight component.
16. The polymer of claim 15 , wherein the ethylene polymer has:
a melt index in a range from about 0.2 to about 0.9.
17. The polymer of claim 11 , wherein the ethylene polymer is an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, or an ethylene/1-octene copolymer.
18. An article comprising the ethylene polymer of claim 11 .
19. A blow molded article comprising the ethylene polymer of claim 11 .
20. An ethylene polymer comprising a higher molecular weight component and a lower molecular weight component, wherein the ethylene polymer has a density of greater than or equal to about 0.95 g/cm 3 , a melt index (MI) in a range from about 0.05 to about 1.5 g/10 min, a ratio of high load melt index to melt index (HLMI/MI) in a range from about 40 to about 175, and a slope of a plot of the viscosity (Pa-sec) versus shear rate (sec −1 ) at 190° C. of the ethylene polymer at 100 sec −1 in a range from about 0.42 to about 0.65, and wherein the lower molecular weight component has a ratio of Mz/Mw in a range from about 1.5 to about 2.8.
21. The polymer of claim 20 , wherein the ethylene polymer has:
a density in a range from about 0.95 to about 0.965 g/cm 3 ;
an ESCR (100% igepal) of at least 1000 hours; and
an ESCR (10% igepal) of at least 200 hours.
22. The polymer of claim 21 , wherein the ethylene polymer is an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, or an ethylene/1-octene copolymer.
23. A blow molded article comprising the ethylene polymer of claim 22 .
24. An ethylene polymer comprising a higher molecular weight component and a lower molecular weight component, wherein the ethylene polymer has a density of greater than or equal to about 0.95 g/cm 3 , a melt index (MI) in a range from about 0.05 to about 1.5 g/10 min, a ratio of high load melt index to melt index (HLMI/MI) in a range from about 40 to about 175, a peak molecular weight (Mp) of the higher molecular weight component in a range from about 650,000 to about 1,100,000 g/mol, a Mp of the lower molecular weight component in a range from about 40,000 to about 80,000 g/mol, a ratio of Mz/Mw of the lower molecular weight component in a range from about 1.5 to about 2.8, and a ratio of Mw/Mn in a range from about 5 to about 18.
25. The polymer of claim 24 , wherein the ethylene polymer has:
a density in a range from about 0.95 to about 0.965 g/cm 3 ;
an ESCR (100% igepal) of at least 1000 hours; and
an ESCR (10% igepal) of at least 200 hours.
26. The polymer of claim 25 , wherein the ethylene polymer is an ethylene/1-butene copolymer, an ethylene/1-hexene copolymer, or an ethylene/1-octene copolymer.
27. A blow molded article comprising the ethylene polymer of claim 26 .