Sulfide solid electrolyte glass, lithium solid state battery and producing method of sulfide solid electrolyte glass
An object of the present invention is to provide a sulfide solid electrolyte glass with high Li ion conductivity. The present invention achieves the above-mentioned object by providing a sulfide solid electrolyte glass comprising Li 4 P 2 S 6 , characterized by having a glass transition point.
1. A sulfide solid electrolyte glass comprising Li 4 P 2 S 6 , wherein the sulfide solid electrolyte glass has a glass transition point of 180° C. to 400° C., and a ratio of a P 2 S 6 4− structure in all anion structures of the sulfide solid electrolyte glass is 50% by mol or more.
2. The sulfide solid electrolyte glass according to claim 1 , wherein the sulfide solid electrolyte glass does not have a peak with a half-value width of 0.64° or less in a range of 32° 20 33° in measurement by an X-ray diffraction method using a CuKα ray.
3. A sulfide solid electrolyte glass comprising Li 4 P 2 S 6 and having a glass transition point of 180° C. to 400° C., wherein the sulfide solid electrolyte glass does not have a peak with a half-value width of 0.64° or less in a range of 32°≦2∝≦33° in measurement by an X-ray diffraction method using a CuKα ray, and a ratio of a P 2 S 6 4− structure in all anion structures of the sulfide solid electrolyte glass is 50% by mol or more.
4. A lithium solid state battery comprising a cathode active material layer containing a cathode active material, an anode active material layer containing an anode active material, and a solid electrolyte layer formed between the cathode active material layer and the anode active material layer;
wherein at least one of the cathode active material layer, the anode active material layer and the solid electrolyte layer contains the sulfide solid electrolyte glass according to claim 1 .
5. A producing method of a sulfide solid electrolyte glass comprising Li 4 P 2 S 6 , comprising:
a synthesis step of synthesizing the sulfide solid electrolyte glass by performing vitrification treatment for a raw material composition containing Li 2 S, a material having a P—P bond and a material having S,
wherein a ratio of a P 2 S 6 4− structure in all anion structures of the sulfide solid electrolyte glass is 50% by mol or more and wherein the sulfide solid electrolyte glass having a glass transition point of 180° C. to 400° C.
6. The producing method of a sulfide solid electrolyte glass according to claim 5 , wherein the material having a P—P bond is elemental phosphorus.
7. The producing method of a sulfide solid electrolyte glass according to claim 5 , wherein the material having S is elemental sulfur.
8. The producing method of a sulfide solid electrolyte glass according to claim 5 , wherein the vitrification treatment is mechanical milling.
9. A lithium solid state battery comprising a cathode active material layer containing a cathode active material, an anode active material layer containing an anode active material, and a solid electrolyte layer formed between the cathode active material layer and the anode active material layer;
wherein at least one of the cathode active material layer, the anode active material layer and the solid electrolyte layer contains the sulfide solid electrolyte glass according to claim 3 .