Magnetically responsive photonic nanochains
View Patent ↗Magnetically responsive photonic nanochains that have been produced by inducing chaining of uniform magnetic particles during their silica coating process and then allowing additional deposited silica to wrap entire structures. The optical diffraction of these nanochains can be switched on and off by applying magnetic fields.
1. A method of fabricating individually fixed nanochains with a magnetically responsive photonic property comprising:
coating a plurality of colloidal nanoclusters with a layer of silica;
applying a magnetic field to the plurality of colloidal nanoclusters to assemble the colloidal nanoclusters into one or more photonic chains; and
overcoating an entirety of each of the one or more photonic chains with an additional layer of silica, which fixes the entirety of each of the one or more photonic chains within a silica shell.
2. The method of claim 1 , wherein the colloidal nanoclusters are superparamagnetic iron oxide (Fe 3 O 4 ) nanocrystal clusters.
3. The method of claim 1 , wherein the step of applying the magnetic field is performed during the coating of the plurality of colloidal nanoclusters with the layer of silica, wherein the layer of silica is an initial layer of silica.
4. The method of claim 1 , wherein the one or more photonic chains are rods and/or wires.
5. The method of claim 1 , comprising:
using colloidal nanoclusters of one or more diameter and/or sizes.
6. The method of claim 1 , comprising:
adjusting a timing of applying the magnetic field to the colloidal nanoclusters to control interparticle spacing between the plurality of colloidal nanoclusters.
7. The method of claim 1 , comprising:
changing a duration of the magnetic exposure to control a length of the photonic chains.
8. The method of claim 1 , wherein the colloidal nanoclusters are superparamagnetic Fe 3 O 4 colloidal nanoclusters synthesized using a high-temperature hydrolysis reaction.
9. The method of claim 8 , wherein the synthesis of the photonic chains comprises:
an aqueous solution of colloidal nanoclusters dispersed in a mixture of NH 4 OH and ethanol under sonication.
10. The method of claim 9 , comprising:
transferring the mixture into a flask under mechanical stirring and injecting TEOS into the mixture.
11. The method of claim 10 , comprising:
transferring the mixture to a glass vial and placing the mixture above a Neodymium disc magnet.
12. The method of claim 11 , comprising:
removing the magnetic field and allowed the mixture to sit undisturbed and washing the mixture with ethanol and redispersing the mixture in ethanol.
13. The method of claim 1 , wherein the magnetic field has a strength of approximately 570 G for particles having a diameter of approximately 160 nm.
14. The method of claim 1 , wherein the step of applying the magnetic field to the plurality of colloidal nanoclusters to assemble the colloidal nanoclusters is performed during the step of coating the plurality of colloidal nanoclusters and before the additional layer of silica, which wraps each of the one or more photonic chains into rods and/or wires.
15. A method of fabricating individually fixed nanochains with a magnetically responsive photonic property comprising:
coating a plurality of colloidal nanoclusters with a layer of silica;
applying a magnetic field to the plurality of colloidal nanoclusters having an initial layer of silica of less than 20 nm, and wherein the plurality of colloidal nanoclusters assemble into one or more photonic chains; and
overcoating each of the one or more photonic chains with an additional layer of silica, which fixes and wraps each of the one or more photonic chains within a silica shell.
16. The method of claim 15 , comprising:
using colloidal nanoclusters of one or more diameter and/or sizes.
17. The method of claim 15 , comprising:
adjusting a timing of applying the magnetic field to the colloidal nanoclusters to control interparticle spacing between the plurality of colloidal nanoclusters.
18. The method of claim 15 , comprising:
changing a duration of the magnetic exposure to control a length of the photonic chains.
19. The method of claim 15 , wherein the colloidal nanoclusters are superparamagnetic Fe 3 O 4 colloidal nanoclusters synthesized using a high-temperature hydrolysis reaction.
20. The method of claim 15 , wherein the colloidal nanoclusters are superparamagnetic iron oxide (Fe 3 O 4 ) nanocrystal clusters, and the one or more photonic chains are rods and/or wires.