Functionalized nanodiamond reinforced biopolymers
The present invention includes a composition for implantation in a patient, comprising surface-functionalized nanodiamonds and at least one biodegradable biocompatible polymer. The present invention also includes a surgical fixation device for use in a patient.
1. A nanocomposite material comprising poly-L-lactic acid (PLLA) and 1-10% by weight of octadecylamine-surface-functionalized nanodiamonds (ND-ODA), wherein ND-ODA has the formula of
and wherein the Young's modulus of the nanocomposite material is between 5.1 and 8.0 GPa.
2. The nanocomposite material of claim 1 , wherein the ND-ODA are prepared by peptide bond formation between octadecylamine and a carboxylate group on the surface-functionalized nanodiamonds.
3. The nanocomposite material of claim 1 , further comprising a composition comprising at least one bioactive agent selected from the group consisting of a bone healing drug, growth factor, bone cell, bone stem cell, antibiotic, and anti-inflammatory drug.
4. The nanocomposite material of claim 1 , wherein the Meyer's hardness of the nanocomposite material is between 0.20 and 0.51 GPa.
5. The nanocomposite material of claim 1 , wherein there is no phase separation of ND-ODA and PLLA.
6. A surgical fixation screw, comprising:
an interconnective porous shell, wherein said shell comprises a nanocomposite material comprising poly-L-lactic acid (PLLA) and 1-10% by weight of octadecylamine-surface-functionalized nanodiamonds (ND-ODA), wherein ND-ODA has the formula of
and wherein the Young's modulus of the nanocomposite material is between 5.1 and 8.0 GPa, and
a hollow core within said shell, wherein said hollow core is closed on the posterior end of said screw and open on the anterior end of said screw.
7. The surgical fixation screw of claim 6 , wherein said hollow core is optionally filled with a composition comprising at least one bioactive agent selected from the group consisting of a bone healing drug, growth factor, bone cell, bone stem cell, antibiotic, and anti-inflammatory drug.
8. The surgical fixation screw of claim 6 , wherein said posterior end is tapered with respect to said anterior end.
9. The surgical fixation screw of claim 8 , wherein said screw has full-length taper.
10. The surgical fixation screw of claim 6 , wherein said anterior end is without head.
11. The surgical fixation screw of claim 6 , wherein said posterior end is rounded and blunt.
12. The surgical fixation screw of claim 6 , wherein said shell has controllable varying coarseness, whereby phase of said nanocomposite material around said hollow core is coarser than phase of said nanocomposite material on outside surface of said screw.
13. The surgical fixation screw of claim 12 , wherein said controllable varying coarseness is achieved through injection molding.
14. A method of performing an orthopedic surgery procedure in a patient, comprising the steps of:
inserting a surgical fixation screw in at least one orifice of a bone or tissue of said patient, wherein said screw comprises:
an interconnective porous shell, wherein said shell comprises a nanocomposite material comprising poly-L-lactic acid (PLLA) and 1-10% by weight of octadecylamine-surface-functionalized nanodiamonds (ND-ODA), wherein ND-ODA has the formula of
and wherein the Young's modulus of the nanocomposite material is between 5.1 and 8.0 GPa, and
a hollow core within said shell, wherein said hollow core is closed on the posterior end of said screw and open on the anterior end of said screw, and
filling said hollow core of said screw with a composition comprising at least one bioactive agent selected from the group consisting of a bone healing drug, growth factor, bone cell, bone stem cell, antibiotic, and anti-inflammatory drug.
15. The method of claim 14 , wherein said posterior end is tapered with respect to said anterior end.
16. The method of claim 15 , wherein said screw has full-length taper.
17. The method of claim 14 , wherein said anterior end is without head.
18. The method of claim 14 , wherein said posterior end is rounded and blunt.
19. The method of claim 14 , wherein said shell has controllable varying coarseness, whereby phase of said nanocomposite material around said hollow core is coarser than phase of said nanocomposite material on outside surface of said screw.
20. The method of claim 19 , wherein said controllable varying coarseness is achieved through injection molding.