Protective fluorine-doped silicon oxide film for optical components
An optical component includes a substrate and a fluorine-doped thin film formed on the substrate. This fluorine-doped thin film is dense, and thus very low absorbing and insensitive to various vacuum, temperature, and humidity conditions. This dense film has a high refractive index, which remains stable irrespective of environmental conditions. The fluorine-doped thin film can advantageously ensure low scattering, low reflectance, and high transmittance. Moreover, the fluorine-doped thin film is damage resistant to incident radiation density. The fluorine-doped thin film may be a fluorine-doped silicon oxide film having a thickness of approximately 1-10 nm and a fluorine concentration of 0.1% to 5%.
1. An optical component comprising:
a substrate; and
a fluorine-doped silicon oxide film formed on the substrate, the fluorine-doped silicon oxide film having a thickness of approximately 1-4 nm and having a fluorine concentration of 0.1% to 5%,
wherein the thickness and the fluorine concentration of the fluorine-doped silicon oxide film are configured to minimize absorption of energy from radiation having a wavelength below 245 nm.
2. The optical component of claim 1 , wherein the optical component forms part of a charge-coupled device (CCD) or a time delay integration (TDI) CCD.
3. The optical component of claim 1 , wherein the substrate comprises a material consisting of at least one of boron, silicon nitride, rhodium, titanium oxide, ruthenium and niobium oxide, and
wherein the fluorine-doped silicon oxide film is adhered to the material.
4. The optical component of claim 1 , wherein the substrate comprises a multilayer mirror comprising molybdenum and silicon disposed in alternating layer.
5. The optical component of claim 1 , further comprising a boron layer disposed between the fluorine-doped silicon oxide film and the substrate.
6. The optical component of claim 1 , wherein the fluorine-doped thin film is configured to have at least one of a hardness greater than 6.5 GPa and a Young's modulus greater than 60 GPa.
7. An anti-reflective coating (ARC) for an optical component operable with at least one of deep ultraviolet (DUV) radiation, vacuum ultraviolet (VUV) radiation, extreme ultraviolet (EUV) radiation, and charged particles, the ARC comprising:
a multilayer substrate including molybdenum and silicon disposed in alternating layers; and
a fluorine-doped silicon oxide film formed on the substrate, the fluorine-doped silicon oxide film having a thickness of approximately 1-10 nm and having a fluorine concentration of 0.1% to 5%.
8. The ARC of claim 7 , wherein the optical component is a beam splitter, a mirror, a detector, or a sensor.
9. The optical component of claim 7 , wherein the fluorine-doped thin film is configured to have at least one of a hardness greater than 6.5 GPa and a Young's modulus greater than 60 GPa.
10. A method of fabricating a protective film for an optical component, the method comprising:
performing a thin film deposition on a silicon substrate to form an oxide; and
introducing fluorine as a dopant during the thin film deposition such that a fluorine-doped silicon oxide film is generated on the oxide, the fluorine-doped silicon oxide film having a thickness of approximately 1-10 nm and having a fluorine concentration of 0.1% to 5% m,
wherein said introducing fluorine includes generating atomic fluorine.
11. The method of claim 10 , wherein said generating atomic fluorine includes dissociating fluorine gas.
12. The method of claim 10 , wherein said performing thin film deposition is one of oxidation, deep ultraviolet oxidation, sol gel methods, ion-assisted deposition, ion beam sputtering, chemical vapor deposition (CVD), plasma enhanced CVD, plasma deposition, thermal evaporation, and electron beam evaporation.