Blends for composite materials

1. A blend, comprising:

(a) an epoxy resin component comprising:

(a1) from 75 to 97 parts by weight, based on epoxy resin component (a), of one or more epoxy resins selected from the group of aromatic epoxy resins and/or cycloaliphatic epoxy resins, and

(a2) from 3 to 18 parts by weight, based on epoxy resin component (a), of one or more cyclic carbonates selected from the group of cyclic carbonates having from 1 to 10 carbon atoms, and

(a3) from 0 to 15 parts by weight, based on epoxy resin component (a), of one or more reactive diluents,

wherein the parts by weight of components (a1) to (a3) always give a total of 100, and

(b) a hardener comprising:

(b 1) from 10 to 79 parts by weight, based on the hardener (b), of one or more polyalkoxypolyamines, and

(b2) from 20 to 89 parts by weight, based on the hardener (b), of one or more other amines selected from the group of aromatic, arylaliphatic, cycloaliphatic, heterocyclic and aliphatic polyamines having at least 3 carbon atoms and at least 4 reactive NH functions in primary and/or secondary amino groups, and

(b3) from 0.5 to 30 parts by weight, based on the hardener (b), of one or more catalysts selected from the group of tertiary amines, imidazoles, imidazolines, guanidines having less than 3 carbon atoms and/or less than 4 reactive NH functions in amino groups, secondary amines having less than 4 reactive NH functions, substituted ureas, guanamines and ketimines,

wherein the parts by weight of components (b1) to (b3) always give a total of 100,

wherein the ratio of amino equivalents of the hardener (b) to the equivalent of the entirety of epoxy resin and cyclic carbonate in epoxy resin component (a) is in the range from 0.3 to 0.9,

wherein the reactive diluents (a3) are selected from the group consisting of 1,4-butanediol bisglycidyl ether, 1,6-hexanediol bisglycidyl ether, glycidyl neodecanoate, glycidyl versatate, 2-ethylhexyl glycidyl ether, C 8 -C 10 -alkyl glycidyl ether, C 12 -C 14 -alkyl glycidyl ether, C 13 -C 15 -alkyl glycidyl ether, p-tert-butyl glycidyl ether, butyl glycidyl ether, nonylphenyl glycidyl ether, p-tert-butylphenyl glycidyl ether, phenyl glycidyl ether, o-cresyl glycidyl ether, polyoxypropylene glycol diglycidyl ether, trimethylolpropane triglycidyl ether, glyceryl triglycidyl ether, triglycidyl paraaminophenol, divinyl benzyl dioxide, dicyclopentadiene diepoxide, and mixtures thereof.

2. The blend according to claim 1 , wherein the epoxy resins (a1) are those selected from the group of bisphenol A bisglycidyl ether and bisphenol F bisglycidyl ether.

3. The blend according to claim 1 , wherein the one or more cyclic carbonates (a2) are propylene carbonate and/or ethylene carbonate.

4. The blend according to claim 1 , wherein the one or more reactive diluents (a3) are those selected from the group of 1,4-butanediol bisglycidyl ether, 1,6-hexanediol bisglycidyl ether, C 12 -C 14 -alkyl glycidyl ether, C 13 -C 15 -alkyl glycidyl ether and trimethylolpropane triglycidyl ether.

5. The blend according to claim 1 , wherein the one or more reactive diluents (a3) are those selected from the group of 1,4-butanediol bisglycidyl ether, 1,6-hexanediol bisglycidyl ether, C 12 -C 14 -alkyl glycidyl ether and C 13 -C 15 -alkyl glycidyl ether.

6. The blend according to claim 1 , wherein the one or more polyalkoxypolyamines (b1) are those selected from the group of Polyetheramin D230, Polyetheramin D 400, Polyetheramin T 403, Polyetheramin T 5000 and aliphatic polyetheramine produced via amination of butylene-oxide-grafted alcohols with average molecular weight 219.

7. The blend according to claim 1 , wherein one or more other amines (b2) are isophoronediamine and/or a mixture of 4-methylcyclohexane-1,3-diamine and 2-methylcyclohexane-1,3-diamine.

8. The blend according to claim 1 , wherein the blend also comprises reinforcement fibers.

9. The blend according to claim 1 , wherein the one or more cyclic carbonates (a2) make up 6 to 18 parts by weight, based on the epoxy resin component (a).

10. The blend according to claim 1 , wherein the one or more catalysts (b3) are selected from the group of tertiary amines and guanidines having less than 3 carbon atoms and/or less than 4 reactive NH functions in amino groups.

11. The blend according to claim 1 , wherein the one or more catalysts (b3) are selected from the group of tertiary amines.

12. The blend according claim 1 , wherein the one or more catalysts (b3) are selected from the group of guanidines having less than 3 carbon atoms and/or less than 4 reactive NH functions in amino groups.

13. The blend according to claim 1 , wherein one or more catalysts (b3) are those selected from the group of tetramethylguanidine, 2,4,6-tris(dimethylaminomethyl)phenol and 1,4-diazabicyclo[2.2.2]octane.

14. The blend according to claim 1 , wherein the one or more catalysts (b3) are selected from the group of 2,4,6-tris(dimethylaminomethyl)phenol and 1,4-diazabicyclo[2.2.2]octane.

15. The blend according to claim 1 , wherein the catalyst (b3) is tetramethylguanidine.

16. The blend according to claim 1 , wherein the one or more catalysts (b3) make up 0.5 to 7 parts by weight, based on the hardener (b).

17. The blend according to claim 1 , wherein the one or more catalysts (b3) make up 0.5 to 7 parts by weight, based on the hardener (b), and are selected from the group of 2,4,6-tris(dimethylaminomethyl)phenol and 1,4-diazabicyclo[2.2.2]octane.

18. The blend according to claim 1 , wherein the catalyst (b3) makes up 0.5 to 7 parts by weight, based on the hardener (b), and is 1,4-diazabicyclo[2.2.2]octane.

19. A process for producing the blend according to claim 1 , wherein epoxy resin component (a) and the hardener (b) are mixed at temperatures below the curing-onset temperature.

20. A process for producing a cured epoxy resin, wherein the blend according to claim 1 is cured at a temperature greater than or equal to the curing-onset temperature.

21. A cured epoxy resin obtainable via curing of the blend according to claim 1 at a temperature greater than or equal to the curing-onset temperature.