Optical cable for communication and process for the manufacturing thereof
It is disclosed an optical cable for communications including at least one micromodule, the micromodule including a retaining element and number N of optical fibers housed in said retaining element. The diameter of a circumference encircling the number N of optical fibers is typically 90% to 95% of an inner diameter of the retaining element. The retaining element consists essentially of a film grade polymeric material having an elongation at break equal to or higher than 500%, a melt flow index (MFI) lower than 3 g/10 min, and a density lower than 1 g/cm 3 .
1. An optical cable for communications ( 5 ), comprising:
at least one micromodule ( 1 ), said micromodule ( 1 ) comprising a retaining element ( 3 ) and a number N of optical fibers ( 2 ) housed in said retaining element ( 3 ), wherein:
a diameter of a circumference (C) encircling said number N of optical fibers ( 2 ) is 90% to 95% of an inner diameter (ID) of said retaining element ( 3 ); and
said retaining element ( 3 ) consists essentially of a film grade polymeric material having an elongation at break equal to or higher than 500%, a melt flow index MFI lower than 3 g/10 min, and a density lower than 1 g/cm 3 .
2. The optical cable according to claim 1 , wherein the retaining element ( 3 ) has a thickness ranging from 0.030 mm to 0.125 mm.
3. The optical cable according to claim 2 , wherein said retaining element ( 3 ) has a thickness ranging from 0.050 mm to 0.110 mm.
4. The optical cable according to claim 1 , wherein said retaining element ( 3 ) is made of a polymeric material having an elongation at break equal to or higher than 600%.
5. The optical cable according to claim 1 , wherein said retaining element ( 3 ) is made of a polymeric material having an elongation at break equal to or higher than 800%.
6. The optical cable according to claim 1 , wherein said film grade polymeric material is uncharged.
7. The optical cable according to claim 1 , wherein said number N of optical fibers is equal to 12, and the outer diameter of said retaining element ( 3 ) ranges from 1.15 mm to 1.3 mm.
8. The optical cable according to claim 1 , wherein said number N of optical fibers is equal to 4, and the outer diameter of said retaining element ( 3 ) ranges from 0.75 mm to 0.89 mm.
9. A micromodule ( 1 ) for an optical cable for communications ( 5 ), comprising:
a retaining element ( 3 ) and a number N of optical fibers ( 2 ) housed in said retaining element ( 3 ), wherein:
a diameter of a circumference (C) encircling said number N of optical fibers ( 2 ) is 90% to 95% of an inner diameter (ID) of said retaining element ( 3 ); and
said retaining element ( 3 ) consists essentially of a film grade material having an elongation at break equal to or higher than 500%, a melt flow index MFI lower than 3 g/10 min, and a density lower than 1 g/cm 3 .
10. The micromodule ( 1 ) according to claim 9 , wherein said retaining element ( 3 ) has a thickness ranging from 0.030 mm to 0.125 mm.
11. The micromodule ( 1 ) according to claim 10 , wherein said retaining element ( 3 ) has a thickness ranging from 0.050 mm to 0.110 mm.
12. The micromodule ( 1 ) according to claim 9 , wherein said retaining element ( 3 ) is made of a polymeric material having an elongation at break equal to or higher than 600%.
13. The micromodule ( 1 ) according to claim 9 , wherein said retaining element ( 3 ) is made of a polymeric material having an elongation at break equal to or higher than 800%.
14. The micromodule ( 1 ) according to claim 9 , wherein said film grade polymeric material is uncharged.
15. The micromodule ( 1 ) according to claim 9 , wherein said number N of optical fibers is equal to 12, and the outer diameter of said retaining element ( 3 ) ranges from 1.15 mm and 1.3 mm.
16. The micromodule ( 1 ) according to claim 9 , wherein said number N of optical fibers is equal to 4, and an outer diameter of said retaining element ( 3 ) ranges from 0.75 mm to 0.89 mm.
17. A process for manufacturing a micromodule ( 1 ) for an optical cable for communications ( 5 ), said process comprising:
providing a number N of optical fibers ( 2 ); and
providing a retaining element ( 3 ) around said number N of optical fibers ( 2 ) thus forming said micromodule ( 1 ),
wherein providing a retaining element ( 3 ) comprises extruding a film grade material, said film grade material having an elongation at break equal to or higher than 500%, a melt flow index MFI lower than 3 g/10 min, and a density lower than 1 g/cm 3 , wherein the diameter of a circumference (C) encircling said number N of optical fibers ( 2 ) is 90% to 95% of an inner diameter (ID) of said retaining element ( 3 ).
18. The process according to claim 17 , wherein said step of extruding is performed by means of extrusion assemblies ( 400 a ) comprising a tip element ( 40 ) and a die element ( 41 ).
19. The process according to claim 18 , wherein said tip element ( 40 ) and said die element ( 41 ) have a draw down ratio DDR ranging from 4.5 to 8.5.
20. The process according to claim 18 , wherein said step of extruding is performed as tubing extrusion.
21. The process according to claim 17 , wherein said step of extruding is performed at a line rate ranging from 40 m/min to 150 m/min.
22. The process according to claim 17 , wherein said film grade material has an elongation at break equal to or higher than 600%.