Methods for variation of support oxide materials for ZPGM oxidation catalysts and systems using same
Disclosed here are methods of preparing zero platinum group metal catalysts systems with different support oxide material. A ZPGM catalyst system may include a substrate and a washcoat and an impregnation layer, wherein said impregnation layer may include the ZPGM pervoskite catalyst and the washcoat layer may include the support oxides material. Suitable support oxides material may include ZrO 2 , ZrO 2 doped with lanthanide group metals, Nb 2 O 5 , Nb 2 O 5 —ZrO 2 , Al 2 O 3 and Al 2 O 3 doped with lanthanide group metals, TiO 2 and doped TiO 2 or mixtures thereof.
1. A catalyst system, comprising:
a substrate;
a washcoat suitable for deposition on the substrate, comprising Praseodymium-doped Zirconium oxide; and
an impregnation layer, comprising at least one second catalyst;
wherein the at least one second catalyst comprises about 1% to about 10% by weight silver about 10% to about 40% by weight lanthanum, and about 10% to about 30% by weight manganese.
2. The catalyst system of claim 1 , wherein the at least one second catalyst comprises about 1% to about 10% by weight silver, about 10% to about 40% by weight lanthanum, and about 10% to about 30% by weight manganese.
3. A catalyst system, comprising:
a substrate:
a washcoat suitable for deposition on the substrate, comprising at least one oxide solid selected from the group consisting of a carrier material oxide, at least one first catalyst, and a mixture thereof; and
an impregnation layer, comprising at least one second catalyst;
wherein the at least one second catalyst includes a perovskite structured compound of the general formula La 1-x Ag x MnO 3 wherein x is from 0 to 1;
wherein the at least one second catalyst comprises about 1% to about 10% by weight silver, about 10% to about 40% by weight lanthanum, and about 10% to about 30% by weight manganese.
4. The catalyst system of claim 3 , wherein the at least one oxide solid is ZrO 2 —Pr 6 O 11 .
5. The catalyst system of claim 4 , wherein the ZrO 2 —Pr 6 O 11 comprises about 80 to about 95 percent by weight ZrO 2 and about 5 to about 20 percent by weight Pr 6 O 11 .
6. The catalyst system of claim 5 , wherein the ZrO 2 —Pr 6 O 11 comprises about 90 percent by weight ZrO 2 and about 10 percent by weight Pr 6 O 11 .