Method for manufacturing display device
A method for manufacturing a display device includes: forming a deformed layer on a support substrate by a silane coupling agent; performing UV treatment on the deformed layer; forming a thin film substrate on the deformed layer; forming a pixel and an encapsulation member on the thin film substrate; and separating the support substrate from the thin film substrate.
1. A method for manufacturing a display device, the method comprising:
forming a separation layer on a support substrate by depositing a silane coupling agent;
performing UV treatment on the separation layer;
forming a thin film substrate on the separation layer;
forming a pixel and an encapsulation member on the thin film substrate; and
separating the support substrate from the thin film substrate by generating bubbles in the separation layer.
2. The method of claim 1 , wherein the formation of the pixel comprises at least one process step which is carried out at a temperature of 300° C. or higher.
3. The method of claim 2 , wherein
the formation of the pixel comprises:
forming a polysilicon layer on the thin film substrate;
forming a semiconductor layer having source and drain regions by doping the polysilicon layer with conductive impurity ions; and
activating the conductive impurity ions,
wherein the activation is carried out at a temperature of 300° C. or higher.
4. The method of claim 1 , further comprising performing heat treatment on the separation layer after the UV treatment.
5. The method of claim 4 , wherein the heat treatment is carried out at a temperature of 300° C. or higher.
6. The method of claim 5 , wherein the heat treatment is carried out at a temperature of 300° C. to 450° C.
7. The method of claim 4 , wherein the heat treatment is carried out for 30 minutes to 1 hour.
8. The method of claim 1 , wherein the silane coupling agent is represented by the following Chemical Formula 1:
(R is an alkyl group having 1 to 20 carbon atoms).
9. The method of claim 8 , wherein the separation layer is formed at a thickness of 1 μm to 3 μm.
10. The method of claim 1 , wherein the UV treatment is carried out for 10 to 30 minutes.
11. The method of claim 1 , wherein the thin film substrate comprises either a polymer substrate or thin film glass substrate comprising at least one selected from the group consisting of polyimide, polycarbonate, polyacrylate, polyetherimide, polyethersulfone, polyethylene terephthalate, and polyethylene naphthalate.
12. The method of claim 11 , wherein the thin film glass substrate has a thickness of 50 μm to 200 μm.
13. The method of claim 11 , wherein
in the formation of the thin film substrate,
the thin film substrate is a polymer substrate, and
the polymer substrate undergoes a dehydration step.
14. The method of claim 13 , wherein the dehydration step is carried out at a temperature of 300° C. or higher.
15. The method of claim 1 , wherein the pixel comprises an organic light emitting diode.