Three-dimensional nanofiber scaffold for tissue repair and preparation method thereof
The present invention provides a three-dimensional nanofibrous scaffold for tissue regeneration, which is increased in porosity and thickness to enlarge the surface area thereof, thereby enabling cell adhesion at a high density, and a method for fabricating the same. The method for fabricating a three-dimensional nanofibrous scaffold for tissue regeneration includes the steps of: (a) preparing a polymer solution; (b) preparing a nanofiber matrix, in which a plurality of nanofibers is entangled with each other, from the polymer solution prepared in step (a) using electrospinning; and (c) immersing the prepared nanofiber matrix in a solution and subjecting the solution to ultrasonication, thereby increasing the thickness and porosity of the nanofiber matrix. According to the inventive scaffold fabricating method, the nanofiber matrix prepared by using electrospinning is ultrasonicated in a solution, so that a three-dimensional nanofibrous scaffold with improved thickness and porosity can be provided in a simple and low-cost manner.
1. A method of fabricating a three-dimensional nanofibrous scaffold for tissue regeneration, the method comprising the steps of:
producing a nanofiber matrix including a plurality of nanofibers entangled with each other from a polymer solution by electrospinning;
immersing the produced nanofiber matrix in a solution;
applying ultrasonication to the solution containing the produced nanofiber matrix, in a state in which the solution is cooled, to expand pores between the plurality of nanofibers and increase a thickness of the produced nanofiber matrix;
coating the expanded nanofiber matrix with a natural polymer; and
freeze-drying the natural polymer-coated nanofiber matrix.
2. The method according to claim 1 , wherein the natural polymer is selected from the group consisting of gelatin and chitosan.
3. The method according to claim 1 , wherein in the step of applying ultrasonication to the solution, the solution is cooled with ice.
4. The method according to claim 1 , wherein in the step of applying ultrasonication to the solution, sonic waves are applied to the solution in a state in which the temperature of the solution is 0° C. to 4° C.
5. The method according to claim 1 , wherein the solution is a natural polymer solution.
6. The method according to claim 5 , wherein the natural polymer solution is selected from the group consisting of an aqueous gelatin solution and an aqueous chitosan solution.
7. The method according to claim 1 , wherein the polymer solution includes a synthetic polymer and a natural polymer.
8. A three-dimensional nanofibrous scaffold for tissue regeneration fabricated by a process comprising the steps of:
producing a nanofiber matrix including a plurality of nanofibers entangled with each other from a polymer solution by electrospinning;
immersing the produced nanofiber matrix in a solution;
applying ultrasonication to the solution containing the produced nanofiber matrix, in a state in which the solution is cooled, to expand pores between the plurality of nanofibers and increase a thickness of the produced nanofiber matrix;
coating the expanded nanofiber matrix with a natural polymer; and
freeze-drying the natural polymer-coated nanofiber matrix.