Methods of preparing polyhemiaminals and polyhexahydrotriazines
Polyhexahydrotriazine (PHT) film layers are formed by a process comprising heating a first mixture comprising i) a solvent, ii) paraformaldehyde, and iii) a diamine monomer comprising two primary aromatic amine groups at a temperature of about 20° C. to less than 150° C. This heating step forms a stable polyhemiaminal (PHA) in solution, which can be cast on a surface of a substrate, thereby forming an initial film layer comprising the PHA. The initial film layer is heated at a temperature of 180° C. to about 280° C., thereby converting the PHA film layer to a PHT film layer. Young's moduli of about 8 GPA to about 14 GPA have been observed for the PHT film layers.
1. A method, comprising:
forming a reaction mixture comprising a i) solvent, ii) paraformaldehyde, and iii) a monomer comprising two primary aromatic amine groups; and
heating the reaction mixture at a temperature of 150° C. to about 280° C., thereby forming a polyhexahydrotriazine (PHT).
2. A method, comprising:
forming a first mixture comprising a i) solvent, ii) paraformaldehyde, and iii) a monomer comprising two primary aromatic amine groups;
heating the first mixture at a temperature of about 20° C. to about 120° C., thereby forming a second mixture comprising a polyhemiaminal (PHA);
casting the second mixture on a surface of a substrate, thereby forming an initial film layer disposed on the surface, the initial film layer comprising the PHA and the solvent; and
heating the initial film layer at a temperature of 150° C. to about 280° C., thereby forming a second film layer comprising a polyhexahydrotriazine (PHT).
3. The method of claim 2 , wherein the solvent is selected from the group consisting of N-methylpyrollidone (NMP), propylene carbonate (PC), dimethylacetamide (DMA), dimethylsulfoxide (DMSO), propylene glycol methyl ether acetate (PGMEA), dimethylformamide (DMF), and combinations thereof.
4. The method of claim 2 , wherein the monomer is selected from the group consisting of 4,4′-oxydianiline (ODA), 4,4′-methylenedianiline (MDA), p-phenylenediamine (PD), 4,4′-(9-fluorenylidenyl)dianiline (FDA), and combinations thereof.
5. The method of claim 2 , wherein said heating the initial film layer is performed at a temperature of about 150° C. to about 220° C.
6. The method of claim 2 , wherein the first mixture further comprises a diluent monomer comprising one primary aromatic amine group.
7. The method of claim 6 , wherein the diluent monomer is N,N-dimethyl-p-phenylenediamine (DPD), and the PHT comprises a plurality of N,N-dimethyl-p-phenylene groups:
wherein the aromatic carbon represented as bonded to an asterisk of the diluent group is covalently linked to a nitrogen of a hexahydrotriazine group.
8. The method of claim 2 , wherein the film layer comprising the PHT has a Young's modulus of about 8 GPa to about 14 GPA.