Radiation-curable ink composition, ink jet recording method, and recorded matter
Provided are a radiation-curable ink composition including phenoxyethyl acrylate (A) in an amount of from 20 to 55 mass % of the total reaction components, a multifunctional acrylate (B) in an amount of from 20 to 50 mass % of the total reaction components, and a black pigment (F1); and a radiation-curable ink composition including phenoxyethyl acrylate (A) in an amount of from 20 to 55 mass % of the total reaction components, a multifunctional acrylate (B) in an amount of from 10 to 50 mass % of the total reaction components, and a yellow pigment (F2).
1. An ink jet recording method comprising the steps of:
(a) discharging a radiation-curable ink composition onto a recording medium, the composition including:
a phenoxyethyl acrylate (A) in an amount of from 20 to 55 mass % of the total reaction components;
a multifunctional acrylate (B) in an amount of from 20 to 50 mass % of the total reaction components;
a black pigment (F1); and
a bis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide photopolymerization initiator in the amount of 5 to 15 parts by mass of the total reaction components; and
(b) irradiating the discharged radiation-curable ink composition with active radiation having a peak emission wavelength ranging from 350 to 400 nm using an active radiation source.
2. The method of claim 1 , wherein the radiation is provided at a dose of from 300 to 1000 mJ/cm 2 .
3. The method of claim 1 , wherein the radiation-curable composition has a viscosity of from 15 to 25 mPa·s.
4. The method according to claim 1 , wherein the multifunctional acrylate (B) is at least one selected from dipropylene glycol diacrylate, tripropylene glycol diacrylate, tetraethylene glycol diacrylate, tricyclodecane dimethanol diacrylate, and propoxylated neopentyl glycol diacrylate.
5. The method according to claim 1 , the ink composition further comprising N-vinyl caprolactam (C) as a reaction component.
6. The method according to claim 1 , the ink composition further comprising a monofunctional acrylate (E) having an alicyclic structure as a reaction component.
7. The method according to claim 6 , wherein the monofunctional acrylate (E) having an alicyclic structure is at least one selected from dicyclopentenyl acrylate, dicyclopentanyl acrylate, and dicyclopentenyloxyethyl acrylate.
8. The method according to claim 1 , the ink composition having a viscosity of from 10 to 40 mPa·s at 20° C. and a surface tension of from 20 to 30 mN/m at 20° C.
9. The method according to claim 1 , wherein the active irradiation source is an LED.
10. An ink jet recording method comprising the steps of:
(a) discharging a radiation-curable ink composition onto a recording medium, the composition including:
a phenoxyethyl acrylate (A) in an amount of from 20 to 55 mass % of the total reaction components;
a multifunctional acrylate (B) in an amount of from 10 to 50 mass % of the total reaction components;
a yellow pigment (F2); and
a bis(2,4,6-tri methylbenzoyl)-phenylphosphine oxide photopolymerization initiator in the amount of 5 to 15 parts by mass of the total reaction components; and
(b) irradiating the discharged radiation-curable ink composition with active radiation having a peak emission wavelength ranging from 350 to 400 nm using an active radiation source.
11. The method of claim 10 , wherein the radiation is provided at a dose of from 300 to 1000 mJ/cm 2 .
12. The method of claim 10 , wherein the radiation-curable composition has a viscosity of from 15 to 25 mPa·s.
13. The method according to claim 10 , wherein the multifunctional acrylate (B) is at least one selected from dipropylene glycol diacrylate, tripropylene glycol diacrylate, tetraethylene glycol diacrylate, tricyclodecane dimethanol diacrylate, and propoxylated neopentyl glycol diacrylate.
14. The method according to claim 10 , the ink composition further comprising N-vinyl caprolactam (C) as a reaction component.
15. The method according to claim 10 , the ink composition further comprising a monofunctional acrylate (E) having an alicyclic structure as a reaction component.
16. The method according to claim 15 , wherein the monofunctional acrylate (E) having an alicyclic structure is at least one selected from dicyclopentenyl acrylate, dicyclopentanyl acrylate, and dicyclopentenyloxyethyl acrylate.
17. The method according to claim 10 , the ink composition having a viscosity of from 10 to 40 mPa·s at 20° C. and a surface tension of from 20 to 30 mN/m at 20° C.
18. The method according to claim 10 , wherein the active irradiation source is an LED.
19. The method according to claim 10 , the ink composition further comprising a thioxanthone-based polymerization initiator.
20. The method according to claim 1 , the ink composition further comprising a thioxanthone-based polymerization initiator.
21. The method according to claim 1 , wherein the ink composition includes the phenoxyethyl acrylate (A) in an amount of from 25 to 55 mass % of the total reaction components.
22. The method according to claim 10 , wherein the ink composition includes the multifunctional acrylate (B) in an amount of from 20 to 32.1 mass % of the total reaction components.