Primer coating for metallized gas barrier films
A primer coating is provided for use on polymeric substrates to enhance the adhesion of metallized coatings to the substrates. The primer coating also improves the gas barrier properties of the substrate when used in combination with a metallized coating. The primer coating includes an amorphous polyvinyl alcohol, polyethyleneimine, and optionally, an aqueous dispersion of polyurethane. The primer coating may be applied to a variety of polymeric substrates including polylactic acid, polyethylene terephthalate, biaxially oriented polyethylene terephthalate, oriented polypropylene, biaxially oriented polypropylene, and biaxially oriented polyamide. When used in combination with the subsequently applied metallized coating, an oxygen transmission rate of about 0.1 and 5.0 cc/m2/day at 0% relative humidity is achieved.
1. A primer coating for enhancing the adhesion of a metallized coating to a polymeric substrate, said coating comprising a blend of an amorphous polyvinyl alcohol, a polyethyleneimine, and an aqueous dispersion of polyurethane.
2. The primer coating of claim 1 comprising about 5 to about 15% by weight of said amorphous polyvinyl alcohol.
3. The primer coating of claim 1 comprising about 0.1 to about 0.15% by weight polyethyleneimine.
4. The primer coating of claim 1 comprising from about from about 0.1 to about 5% by weight of the aqueous dispersion of polyurethane having a solids content of about 33% by weight.
5. The primer coating of claim 1 comprising from about 0.03 to 2.5% by weight the aqueous dispersion of polyurethane having a solids content of about 33 to about 50% by weight.
6. The primer coating of claim 1 further comprising a wetting agent.
7. The primer coating of claim 1 comprising a blend of:
from about 5 to 15% by weight amorphous polyvinyl alcohol;
from about 0.01 to about 0.15% by weight polyethyleneimine;
from about 0.1 to about 5% by weight of an aqueous dispersion of polyurethane having a solids content of about 33% by weight; and
the balance water.
8. A coated polymeric substrate having first and second major surfaces, comprising:
a primer coating comprising amorphous polyvinyl alcohol, a polyethyleneimine, and optionally, a polyurethane coated on at least one of the first and second major surfaces, and
a metallized coating disposed on the primer coating.
9. The coated polymeric substrate of claim 8 wherein said primer coating and metallized coating, in combination, exhibit an oxygen transmission rate of about 0.1 and 5.0 cc/m 2 /day at 0% relative humidity.
10. The coated polymeric substrate of claim 8 wherein said primer coating has a thickness of from between about 0.06 to about 2.27 μm.
11. A method of applying a primer coating to a polymeric substrate for enhancing the adhesion of a metallized coating thereto comprising:
providing a polymeric substrate having first and second major surfaces; and
applying a primer coating to at least one of the first and second major surfaces of said substrate; said coating comprising a blend of amorphous polyvinyl alcohol, polyethyleneimine, and an aqueous dispersion of polyurethane.
12. The method of claim 11 further comprising depositing a metallized coating over said primer coating.
13. The method of claim 12 wherein said metallized coating comprises aluminum.
14. The method of claim 11 further comprising stretching said primer coated polymeric substrate prior to applying said metallized coating.
15. The method of claim 11 including treating said at least one major surface of said substrate by a corona discharge treatment prior to applying said primer coating.
16. A method of applying a primer coating to a polymeric substrate for enhancing the adhesion of a metallized coating thereto comprising:
providing a polymeric substrate having first and second major surfaces;
applying a primer coating to at least one of the first and second major surfaces of said substrate; said coating comprising a blend of amorphous polyvinyl alcohol, polyethyleneimine, and optionally, an aqueous dispersion of polyurethane; and
depositing the metallized coating.