Process for producing polycondensation polymer, and polymerizer

1. A method for producing a condensation polymerization reaction polymer, comprising a guide polymerization step in which a molten prepolymer is supplied to the top edge of a wire guide in a polymerization reactor for production of a condensation polymerization reaction polymer, and is allowed to drop while contacting the wire guide in conducting polymerization of the molten prepolymer and to obtain the condensation polymerization reaction polymer,

the wire guide comprising a vertical wire group comprising a plurality of vertical wires extending in the vertical direction, which are mutually spaced in alignment at an arrangement pitch L 1 (mm), wherein:

in the guide polymerization step,

the molten prepolymer supplied from the top edge of the wire guide aggregates so that a molten prepolymer mass is formed on the vertical wire, and

a molten prepolymer mass is formed wherein, the width of the molten prepolymer mass measured in an alignment direction of the vertical wires at a position 200 mm below the top edge being represented as L 2 (mm), the width L 2 (mm) of at least a portion of the molten prepolymer mass satisfies the relationship with L 1 (mm) as defined by inequality (1),

L1<L2  (1).

2. The method according to claim 1 , wherein L 2 is at least 3-fold of L 1 .

3. The method according to claim 1 , wherein the wire guide comprises a plurality of anchoring wires that link the plurality of vertical wires of the vertical wire group and anchor the positional relationship between the vertical wires, and an arrangement pitch L 5 (mm) of the anchoring wires is at least 1.5-fold of L 1 , and L 1 is 3-20 mm.

4. The method according to claim 1 , characterized by satisfying the relationship between S 1 and S 2 as defined by the following inequality (7),

(S2/S1)<0.05  (7)

wherein the total area of the wire guide as seen from a horizontal direction perpendicular to an alignment direction of the vertical wires is represented by S 1 (mm 2 );

the average thickness of the molten prepolymer mass formed on the wire guide is represented as T 2 (mm); and

the area of thin sections as seen from a horizontal direction perpendicular to an alignment direction of the vertical wires are represented by S 2 (mm 2 ) when a section of the molten prepolymer mass having a thickness of no greater than ⅓ of T 2 are the thin sections.

5. The method according to claim 1 , wherein the relationship between a viscosity η (poise) of the molten prepolymer supplied to the top edge of the wire guide and L 1 (mm) satisfies inequality ( 4 ),

1< L 1<0.11×η±15  (4).

6. The method according to claim 1 , wherein the condensation polymerization reaction polymer is an aromatic polycarbonate.

7. The method for producing a condensation polymerization reaction polymer according to claim 1 , wherein a wire guide for production of a condensation polymerization reaction polymer is employed to obtain the condensation polymerization reaction polymer by conducting polymerization of the polymerization material composed of a molten prepolymer allowed to drop down while in contact, in a polymerization reactor for production of a condensation polymerization reaction polymer,

the wire guide comprising a vertical wire group comprising a plurality of vertical wires that extend in the vertical direction and are mutually spaced in alignment, and an anchoring wire that links the plurality of vertical wires of the vertical wire group and anchors a positional relationship between the vertical wires,

wherein, assuming a tabular virtual space containing the vertical wire group while extending in an alignment direction of the vertical wires, and delineation by a pair of virtual vertical planes sandwiching the vertical wire group,

the anchoring wire extends along a virtual vertical plane outside of the virtual space while being anchored to the plurality of vertical wires of the vertical wire group on the virtual vertical plane, and lies only on the side of one of the virtual vertical planes of the virtual space.

8. A method for producing a condensation polymerization reaction polymer wherein a polymerization material composed of a molten prepolymer is allowed to drop down in a polymerization reactor while in contact with a wire guide extending in the vertical direction, for polymerization of the polymerization material, to obtain a condensation polymerization reaction polymer,

wherein the wire guide is disposed in the polymerization reactor,

the wire guide comprising a vertical wire group comprising a plurality of vertical wires that extend in the vertical direction and mutually spaced in alignment, and an anchoring wire that links the plurality of vertical wires of the vertical wire group and anchors the positional relationship between the vertical wires, wherein

assuming a tabular virtual space containing the vertical wire group while extending in an alignment direction of the vertical wires, and delineation by a pair of virtual vertical planes sandwiching the vertical wire group, and

the anchoring wire extends along a virtual vertical plane outside of the virtual space while being anchored to the plurality of vertical wires of the vertical wire group on the virtual vertical plane.

9. The method for producing a condensation polymerization reaction polymer according to claim 8 , wherein

the polymerization reactor comprises a starting material feed port, a starting material feed zone communicating with the starting material feed port, a guide-contacted dropping polymerization reaction zone located at a lower section of the starting material feed zone and communicating with the starting material feed zone, and a polymer discharge port located at a lower section of the guide-contacted dropping polymerization reaction zone, wherein

the guide-contacted dropping polymerization reaction zone is provided with the wire guide that allows the polymerization material supplied from the starting material feed zone to drop down while in contact therewith for polymerization of the polymerization material, wherein

the polymerization reactor comprises a plurality of the wire guides, each of the wire guides is arranged in an arrangement pitch of L 3 (mm) in a direction perpendicular to an alignment direction of the vertical wires, and the relationship between an arrangement pitch L 1 (mm) of the vertical wires and L 3 satisfies inequality (2):

2× L 1< L 3  (2).

10. The method for producing a condensation polymerization reaction polymer according to claim 8 , wherein

the polymerization reactor comprising a starting material feed port, a starting material feed zone communicating with the starting material feed port, a guide-contacted dropping polymerization reaction zone located at a lower section of the starting material feed zone and communicating with the starting material feed zone, and a polymer discharge port located at a lower section of the guide-contacted dropping polymerization reaction zone, wherein

the guide-contacted dropping polymerization reaction zone is provided with the wire guide that allows the polymerization material supplied from the starting material feed zone to drop down while in contact therewith for polymerization of the polymerization material, wherein

the polymerization reactor further comprises a plurality of polymer feed holes that are provided at the top edge of the polymerization reaction zone in which the wire guide is housed and that feed the molten prepolymer to the top edge of the wire guide,

the polymer feed holes are arranged at an arrangement pitch of L 4 (mm) in an alignment direction of the vertical wires, vertically above the wire guide, and

the relationship between L 4 and an arrangement pitch L 1 (mm) of the vertical wires satisfies inequality (3):

L4>L1  (3).