Ni—Fe—Cr alloy and engine valve welded with the same alloy
A hard-facing alloy having impact resistance, wear resistance and hot corrosion resistance and containing Fe which is a bountiful resource and inexpensive is provided. Provided are: a Ni—Fe—Cr alloy containing 0 to 20.0 mass % of Mo, 8.0 to 40.0 mass % of W, 20.0 to 40.0 mass % of a total amount of Mo and W, 20.0 to 50.0 mass % of Fe, 12.0 to 36.0 mass % of Cr and 1.0 to 2.5 mass % of B, and the remainder being Ni and unavoidable impurities; and an engine valve welded with the same alloy. The above Ni—Fe—Cr alloy can further contain 15 mass % or less of a total amount of elements selected from Co, Mn, Cu, Si and C, in such cases, 15.0 mass % or less of Co, 5.0 mass % or less of each of Mn and Cu, 2.0 mass % or less of Si and 0.5 mass % or less of C are preferred.
1. An engine valve welded or coated with a Ni—Fe—Cr alloy consisting of 0 to 20.0 mass % of Mo, 8.0 to 40.0 mass % of W, 20.0 to 40.0 mass % of a total amount of Mo and W, 20.0 to 50.0 mass % of Fe, 12.0 to 36.0 mass % of Cr, 1.0 to 2.5 mass % of B, 10.4 mass % or more of Ni, and unavoidable impurities.
2. The engine valve according to claim 1 , wherein at least a seat surface coming into contact with a seat insert is welded or coated with said Ni—Fe—Cr alloy.
3. An engine valve welded or coated with a Ni—Fe—Cr alloy consisting of 0 to 20.0 mass % of Mo, 8.0 to 40.0 mass % of W, 20.0 to 40.0 mass % of a total amount of Mo and W, 20.0 to 50.0 mass % of Fe, 12.0 to 36.0 mass % of Cr, 1.0 to 2.5 mass % of B, at least one element selected from Co, Mn, Si and C, 10.4 mass % or more of Ni, and unavoidable impurities, wherein a total amount of Co, Mn, Si and C is 15 mass % or less, the content of Co is 15.0 mass % or less, the content of Mn is 5.0 mass % or less, the content of Si is 2.0 mass % or less, and the content of C is 0.5 mass % or less.
4. The engine valve according to claim 3 , wherein at least a seat surface coming into contact with a seat insert is welded or coated with said Ni—Fe—Cr alloy.
5. An engine valve welded or coated with a Ni—Fe—Cr alloy consisting of 22.0 to 40.0 mass % of W, 20.0 to 50.0 mass % of Fe, 12.0 to 36.0 mass % of Cr, 1.0 to 2.5 mass % of B, 10.4 mass % or more of Ni, and unavoidable impurities.
6. The engine valve according to claim 5 , wherein at least a seat surface coming into contact with a seat insert is welded or coated with said Ni—Fe—Cr alloy.
7. An engine valve welded or coated with a Ni—Fe—Cr alloy consisting of 22.0 to 40.0 mass % of W, 20.0 to 50.0 mass % of Fe, 12.0 to 36.0 mass % of Cr, 1.0 to 2.5 mass % of B, at least one element selected from Co, Mn, Si and C, 10.4 mass % or more of Ni, and unavoidable impurities, wherein a total amount of Co, Mn, Si and C is 15 mass % or less, the content of Co is 15.0 mass % or less, the content of Mn is 5.0 mass % or less, the content of Si is 2.0 mass % or less, and the content of C is 0.5 mass % or less.
8. The engine valve according to claim 7 , wherein at least a seat surface coming into contact with a seat insert is welded or coated with said Ni—Fe—Cr alloy.
9. A Ni—Fe—Cr alloy consisting of 22.0 to 40.0 mass % of W, 20.0 to 50.0 mass % of Fe, 12.0 to 36.0 mass % of Cr, 1.0 to 2.5 mass % of B, 10.4 mass % or more of Ni, and unavoidable impurities.