Ferromagnetic particles and process for producing the same, and anisotropic magnet, bonded magnet and compacted magnet
Ferromagnetic particles including an Fe 16 N 2 compound phase in an amount of not less than 80% as measured by Mössbauer spectrum and each having an outer shell in which FeO is present in the form of a film having a thickness of not more than 5 nm. Ferromagnetic particles may be made by subjecting iron oxide or iron oxyhydroxide having an average major axis diameter of 40 to 5000 nm and an aspect ratio (major axis diameter/minor axis diameter) of 1 to 200 as a starting material to dispersing treatment to prepare aggregated particles; subjecting the iron compound particles passed through a mesh to hydrogen reducing treatment at a temperature of 160 to 420° C.; and then subjecting the resulting particles to nitridation treatment at a temperature of 130 to 170° C.
1. A process for producing ferromagnetic particles comprising an Fe 16 N 2 compound phase in an amount of not less than 80% as measured by Mössbauer spectrum, and each having an outer shell in which FeO is present in the form of a film having a thickness of not more than 5 nm, the process comprising the steps of:
subjecting iron oxide or iron oxyhydroxide having an average major axis diameter of 40 to 5000 nm and an aspect ratio (major axis diameter/minor axis diameter) of 1 to 200 as a starting material to dispersing treatment to prepare aggregated particles having D50 of not more than 40 μm and D90 of not more than 150 μm;
allowing the obtained aggregated particles to pass through a mesh having a size of not more than 250 μm;
subjecting the iron compound particles passed through the mesh to hydrogen reducing treatment at a temperature of 160 to 420° C.; and
then subjecting the resulting particles to nitridation treatment at a temperature of 130 to 170° C.
2. The process for producing ferromagnetic particles according to claim 1 , wherein a saturation magnetization value as of the ferromagnetic particles as measured at 5 K is not less than 150 emu/g.
3. The process for producing ferromagnetic particles according to claim 1 , wherein a volume fraction of the FeO in the ferromagnetic particles is controlled such that a ratio of a volume of the FeO to a whole volume of the particles is not more than 25%.
4. The process for producing ferromagnetic particles according to claim 1 , wherein a coercive force He of the ferromagnetic particles is not less than 1.5 kOe.
5. The process for producing ferromagnetic particles according to claim 1 , wherein a nitridation rate of the ferromagnetic particles is 8.0 to 13 mol %, wherein the nitridation rate is determined from a lattice constant of the ferromagnetic particles.
6. The process for producing ferromagnetic particles according to claim 1 , wherein a BET specific surface area of the ferromagnetic particles is 5.0 to 40 m 2 /g.