Lithium silicate glass ceramic and lithium silicate glass comprising a hexavalent metal oxide
Lithium silicate glass ceramics and glasses containing specific oxides of hexavalent elements are described which crystallize at low temperatures and are suitable in particular as dental materials.
1. Lithium silicate glass ceramic which comprises a hexavalent metal oxide selected from MoO 3 , WO 3 and mixtures thereof and which has lithium metasilicate as main crystal phase.
2. Glass ceramic according to claim 1 , wherein lithium silicate glass ceramic is excluded which comprises at least 6.1 wt.-% ZrO 2 .
3. Glass ceramic according to claim 1 , wherein lithium silicate glass ceramic is excluded which comprises at least 8.5 wt.-% transition metal oxide selected from the group consisting of oxides of yttrium, oxides of transition metals with an atomic number from 41 to 79 and mixtures of these oxides.
4. Glass ceramic according to claim 1 , which comprises less than 2.01 wt.-% K 2 O.
5. Glass ceramic according to claim 1 , which comprises less than 1.0 wt.-% further alkali metal oxide.
6. Glass ceramic according claim 1 , which comprises the hexavalent metal oxide or mixtures thereof in an amount of from 0.1 to 8.4 wt.-%.
7. Glass ceramic according to claim 1 , which comprises 60.0 to 85.0 wt.-% SiO 2 .
8. Glass ceramic according to claim 1 , which comprises 12.0 to 20.0 wt.-% Li 2 O.
9. Glass ceramic according to claim 1 , which comprises 0 to 10.0 wt.-% P 2 O 5 .
10. Glass ceramic according to claim 1 , which comprises at least one of the following components:
Component
wt.-%
SiO 2
69.0 to 77.0
Li 2 O
12.0 to 20.0
hexavalent metal
2.0 to 5.0
oxide or mixtures
P 2 O 5
0 to 7.0
Al 2 O 3
0 to 6.0.
11. Lithium silicate glass ceramic according to claim 1 , which comprises SiO 2 and Li 2 O in a molar ratio of from 1.7 to 3.1.
12. Glass ceramic according to claim 1 wherein the glass ceramic is present in the form of a powder, a granular material, a blank or a dental restoration.
13. Glass ceramic according to claim 1 , wherein the lithium metasilicate as the main crystal phase has more than 5 vol.-%, lithium metasilicate crystals.
14. Process for the preparation of the glass ceramic according to claim 1 , wherein a starting glass, a glass with nuclei, or the glass ceramic with lithium metasilicate as a main crystal phase is subjected to at least one heat treatment in the range of from 450 to 950° C.
15. Process according to claim 14 , wherein
(a) the starting glass is subjected to a heat treatment at a temperature of from 480 to 500° C. in order to form the glass with nuclei, and
(b)the glass with nuclei is subjected to a heat treatment at a temperature of from 520 to 750° C. in order to form the glass ceramic with lithium disilicate as main crystal phase.
16. Method of using the glass ceramic according to claim 1 as dental material for the preparation of dental restorations.
17. Method of preparing the dental restorations according to claim 16 , wherein the glass ceramic or a glass which comprises the components of the glass ceramic is shaped by pressing or machining to the desired dental restoration.