Metal structure catalyst and preparation method thereof
Provided are a metal structure catalyst and a method of preparing the same. Particularly, the method includes forming a metal precipitate on a metal support by contact of a mixed solution including a precursor of a metal catalyst and a precipitating agent with the metal support, and forming metal particles by thermally treating and reducing the metal precipitate formed on the metal support. The metal structure catalyst includes a metal support, a metal oxide layer formed on the metal support, and metal nanoparticles formed on the metal oxide layer. In addition, the metal nanoparticles are uniform and have enhanced binding strength.
1. A method of preparing a metal structure catalyst comprising the steps of:
directly forming a metal precipitate on a metal support by direct contact of a mixed solution with the metal support, the mixed solution including a precursor of a metal catalyst and a precipitating agent being an ammonia solution; and
forming metal particles by thermally treating and reducing the metal precipitate formed on the metal support;
wherein the metal catalyst is nickel;
wherein the forming of the metal precipitate is performed at 60 to 100° C. for 10 to 90 hours.
2. The method according to claim 1 , wherein a precursor solution of the metal catalyst is at least one selected from the group consisting of a metal nitrate, a metal halide, a metal acetate, a metal sulfate, a metal acetoacetate, a metal fluoroacetoacetate, a metal perchlorate, a metal sulfamate, a metal stearate, a metal phosphate, a metal carbonate, a metal oxalate and a metal complex.
3. The method according to claim 1 , wherein the precipitating agent controls a pH of the mixed solution to 8 to 14.
4. The method according to claim 1 , wherein the precipitating agent is used at 100 to 500 parts by volume with respect to 100 parts by volume of the metal precursor solution.
5. The method according to claim 1 , wherein the metal support is one metal or an alloy of at least two metals selected from stainless steel, a FeCr alloy, aluminum and titanium.
6. The method according to claim 1 , wherein the metal support is formed in a type of a felt, mat, mesh, foam, foil or monolith.
7. The method according to claim 1 , wherein the metal support is formed by performing electrochemical surface treatment, and thermal treatment in an oxidation atmosphere.
8. The method according to claim 7 , wherein the metal support is formed by further coating a carrier after the thermal treatment.
9. The method according to claim 8 , wherein the carrier is alumina, boehmite, titania, silica or a ceria-zirconia mixture.
10. The method according to claim 1 , wherein the precipitate is a metal hydroxide or a metal carbonate.
11. The method according to claim 1 , wherein the metal particles are metal oxide nanoparticles.
12. The method according to claim 1 , wherein the thermal treatment is performed at 300 to 900° C. in an oxidation or reduction atmosphere.