All-solid lithium ion secondary battery
To provide an all-solid lithium ion secondary battery having a high voltage, a small internal resistance, and a discharge capacity close to a theoretical capacity and being able to be produced at low cost, and therefore, even in the case of collective sintering, generation of an inactive material due to interface reaction at the interface between an electrode active material and a solid electrolyte is reduced. An all-solid lithium ion secondary battery including a positive electrode layer, a negative electrode layer, and a solid electrolyte layer disposed between the positive electrode layer and the negative electrode layer, wherein an electrode active material included in the positive electrode layer is a phosphate having an olivine structure; and a solid electrolyte crystal included in the solid electrolyte layer includes polyphosphoric acid and the content of Li 2 O is 16 mol % to 25 mol % in terms of mol % on an oxide basis.
1. An all-solid lithium ion secondary battery comprising a positive electrode layer, a negative electrode layer, and a solid electrolyte layer disposed between the positive electrode layer and the negative electrode layer, wherein
an electrode active material included in the positive electrode layer is a phosphate having an olivine structure;
a solid electrolyte crystal included in the solid electrolyte layer is polyphosphate-containing NASICON-type Li 1+x M y Zr 2−y Si z P 3−z O 12+a , and a content of Li 2 O is 16 mol % to 25 mol % in terms of mol % on an oxide basis,
where M is at least one selected from Al, La, Sr, Mg, Y, Ba, Zn, Sc, and Ca, x is 0.1 to 1.2, y is 0.1 to 1.1, z is 0.1 to 1.0, and a is −1.0 to 1.0.
2. The all-solid lithium ion secondary battery according to claim 1 , wherein a solid electrolyte crystal included in the solid electrolyte layer is NASICON-type Li 1+x M y Zr 2−y Si z P 3−z O 12+a ,
where M is at least one selected from Mg, Ca, and Sr, x is 0.1 to 1.2, y is 0.1 to 0.55, z is 0.1 to 1.0, and a is −1.0 to 1.0.
3. The all-solid lithium ion secondary battery according to claim 1 , wherein an electrode active material included in the positive electrode layer, an electrode active material included in the negative electrode layer, and a solid electrolyte crystal included in the solid electrolyte layer have crystal structures differing from each other.
4. The all-solid lithium ion secondary battery according to claim 1 , wherein an electrode active material included in the positive electrode layer is Li n M′PO 4 ,
where M′ is at least one selected from Fe, Co, Mn, Ni, Al, Mg, Ca, Ti, and Zr and n is 0.7 to 1.5.
5. The all-solid lithium ion secondary battery according to claim 1 , wherein an electrode active material included in the negative electrode layer is Li 4 Ti 5 O 12 , anatase-type TiO 2 , or NASICON-type Li 1+x Ti 2−x (PO 4 ) 3 .
6. The all-solid lithium ion secondary battery according to claim 1 , wherein at least one of the positive electrode layer, the negative electrode layer, and the solid electrolyte layer includes 2 to 15% by weight of a lithium ion conductive glass.
7. The all solid lithium ion secondary battery according to claim 1 , wherein
at least one of the positive electrode layer, the negative electrode layer and the solid electrolyte layer contains 2 to 15% by weight of glass comprising Li 2 O, Al 2 O 3 and P 2 O 5 .
8. The all-solid lithium ion secondary battery according to claim 7 , wherein an electrode active material included in the positive electrode layer, an electrode active material included in the negative electrode layer, and a solid electrolyte crystal included in the solid electrolyte layer have crystal structures differing from each other.
9. The all-solid lithium ion secondary battery according to claim 7 , wherein an electrode active material included in the positive electrode layer is Li n M′PO 4 , where M′ is at least one selected from Fe, Co, Mn, Ni, Al, Mg, Ca, Ti, and Zr and n is 0.7 to 1.5.
10. The all-solid lithium ion secondary battery according to claim 7 , wherein an electrode active material included in the negative electrode layer is Li 4 Ti 5 O 12 , anatase-type TiO 2 , or NASICON-type Li 1+x Ti 2−x (PO 4 ) 3 .
11. The all-solid lithium ion secondary battery according to claim 7 , wherein at least one of the positive electrode layer and the negative electrode layer includes acetylene black.
12. The all-solid lithium ion secondary battery according to claim 1 , wherein at least one of the positive electrode layer and the negative electrode layer includes acetylene black.
13. An all-solid lithium ion secondary battery comprising a positive electrode layer, a negative electrode layer, and a solid electrolyte layer disposed between the positive electrode layer and the negative electrode layer, wherein
an electrode active material included in the positive electrode layer is a phosphate having an olivine structure;
a solid electrolyte crystal included in the solid electrolyte layer is polyphosphate-containing NASICON-type Li 1+x M y Zr 2−y Si z P 3−z O 12+a , and a content of Li 2 O is 16 mol % to 25 mol % in terms of mol % on an oxide basis,
where M is at least one selected from Mg, Ca, and Sr, R is at least one selected from Ge, Ti, and Zr, x is 0.1 to 1.2, y is 0.1 to 0.55, z is 0.1 to 1.0, and a is −1.0 to 1.0.
14. The all-solid lithium ion secondary battery according to claim 13 , wherein an electrode active material included in the positive electrode layer, an electrode active material included in the negative electrode layer, and a solid electrolyte crystal included in the solid electrolyte layer have crystal structures differing from each other.
15. The all-solid lithium ion secondary battery according to claim 13 , wherein an electrode active material included in the positive electrode layer is Li n M′PO 4 ,
where M′ is at least one selected from Fe, Co, Mn, Ni, Al, Mg, Ca, Ti, and Zr and n is 0.7 to 1.5.
16. The all-solid lithium ion secondary battery according to claim 13 , wherein an electrode active material included in the negative electrode layer is Li 4 Ti 5 O 12 , anatase-type TiO 2 , or NASICON-type Li 1+x Ti 2−x (PO 4 ) 3 .
17. The all-solid lithium ion secondary battery according to claim 13 , wherein at least one of the positive electrode layer, the negative electrode layer, and the solid electrolyte layer includes 2 to 15% by weight of a lithium ion conductive glass.
18. The all-solid lithium ion secondary battery according to claim 13 , wherein at least one of the positive electrode layer and the negative electrode layer includes acetylene black.
19. The all-solid lithium ion secondary battery according to claim 13 , wherein at least one of the positive electrode layer, the negative electrode layer and the solid electrolyte layer contains 2 to 15% by weight of glass comprising Li 2 O, Al 2 O 3 and P 2 O 5 .
20. The all-solid lithium ion secondary battery according to claim 19 , wherein an electrode active material included in the positive electrode layer, an electrode active material included in the negative electrode layer, and a solid electrolyte crystal included in the solid electrolyte layer have crystal structures differing from each other.
21. The all-solid lithium ion secondary battery according to claim 19 , wherein an electrode active material included in the positive electrode layer is Li n M′PO 4 , where M′ is at least one selected from Fe, Co, Mn, Ni, Al, Mg, Ca, Ti, and Zr and n is 0.7 to 1.5.
22. The all-solid lithium ion secondary battery according to claim 19 , wherein an electrode active material included in the negative electrode layer is Li 4 Ti 5 O 12 , anatase-type TiO 2 , or NASICON-type Li 1+x Ti 2−x (PO 4 ) 3 .
23. The all-solid lithium ion secondary battery according to claim 19 , wherein at least one of the positive electrode layer and the negative electrode layer includes acetylene black.