Adhesive comprising partly hydrolyzed proteins and metal silicates

1. A process for at least partly adhering at least two parts together with a liquid adhesive composition, the process comprising:

placing a liquid adhesive composition having a solid content in the range of 15-80% (w/w) between at least two parts, wherein the liquid adhesive composition is obtained by:

hydrolyzing a protein component to a degree of hydrolysis (DH) in the range of 0.4-0.7, as measured by the “pH stat” method; and

mixing 10-50% (w/w) of the hydrolyzed protein component with 2-60% (w/w) of a metal silicate component; and

pressing the at least two parts together such that the at least two parts are at least partly adhered together by the liquid adhesive composition.

2. The process according to claim 1 , wherein said two parts are selected from the group consisting of plywood, particle board, chip board, medium density fibreboard (MDF), LDF, HDF, oriented strand board (OSB), Veneer, laminated veneer lumber (LVL), laminated strand lumber (LSL), and any combination thereof.

3. The process according to claim 1 , further comprising curing said at least partly adhered at least two parts for a period of at least 1minute at a temperature in the range 50-200° C.

4. The process according to claim 1 , wherein the liquid adhesive composition comprises an exogenic protein hydrolyzing component.

5. The process according to claim 1 , wherein the metal silicate component is selected from the group consisting of sodium silicate, potassium silicate and lithium silicate.

6. reviously Presented) The process according to claim 1 , wherein the degree of hydrolysis is the average degree of hydrolysis of the protein component.

7. The process according to claim 1 , wherein the liquid adhesive composition is substantially or completely free from formaldehyde.

8. The process according to claim 1 , wherein the liquid adhesive composition has an Internal Bond Strength (“IB”) of at least 0.5N/mm 2 (MPa).

9. The process according to claim 1 , wherein the liquid adhesive composition has a viscosity below 1200 cP.

10. A process for at least partly adhering at least two parts together with a liquid adhesive composition, the process comprising:

placing a liquid adhesive composition having a solid content in the range of 15-80% (w/w) between at least two parts, wherein the liquid adhesive composition further comprises:

10-50% (w/w) of a hydrolyzed protein component having a degree of hydrolysis (DH) in the range of 0.4-0.7, as measured by the “pH stat” method; and

2-60% (w/w) of a metal silicate component, wherein the hydrolyzed protein component and the metal silicate component of the liquid adhesive composition are mixed; and

pressing the at least two parts together such that the at least two parts are at least partly adhered together by the liquid adhesive composition.

11. The process according to claim 10 , wherein said two parts are selected from the group consisting of plywood, particle board, chip board, medium density fibreboard (MDF), LDF, HDF, oriented strand board (OSB), Veneer, laminated veneer lumber (LVL), laminated strand lumber (LSL), and any combination thereof.

12. The process according to claim 10 , further comprising curing said at least partly adhered at least two parts for a period of at least 1 minute at a temperature in the range 50-200° C.

13. The process according to claim 10 , wherein the liquid adhesive composition comprises an exogenic protein hydrolyzing component.

14. The process according to claim 10 , wherein the metal silicate component is selected from the group consisting of sodium silicate, potassium silicate and lithium silicate.

15. The process according to claim 10 , wherein the degree of hydrolysis is the average degree of hydrolysis of the protein component.

16. The process according to claim 10 , wherein the liquid adhesive composition is substantially or completely free from formaldehyde.

17. The process according to claim 10 , wherein the liquid adhesive composition has an Internal Bond Strength (“IB”) of at least 0.5 N/mm 2 (MPa).

18. The process according to claim 10 , wherein the liquid adhesive composition has a viscosity below 1200 cP.