Method for producing heterogeneous catalysts containing metal nanoparticles
A monomer is added to a solvent containing metal salt and porous support materials and the solvent is stirred for a period of time to distribute and fix the metal in the pores of the support materials. The solids that are dispersed in the solvent are then separated from the liquid, dried and calcined to form heterogeneous catalysts. The monomer that is added is of a type that can be polymerized in the solvent to form oligomers or polymers, or both. When forming heterogeneous catalysts containing platinum, acrylic acid is selected as the preferred monomer.
1. A method for producing a supported catalyst, comprising:
mixing a metal oxide support material with a metal salt in a solvent;
adding a monomer to the solvent containing metal salt and the metal oxide support materials, the monomer being of a type that can be polymerized in the solvent to form oligomers or polymers, or both;
reducing the metal salt using the monomer by stirring the solvent containing the metal salt, the support materials and the monomer;
separating the liquid from the solid in the solvent; and
calcining the separated solid to produce the supported catalyst.
2. The method according to claim 1 , wherein the monomer comprises acrylic acid.
3. The method according to claim 2 , wherein the metal salt comprises platinum salt and the support materials are made of lanthanum-doped alumina.
4. The method according to claim 1 , further comprising the step of adding a fixing agent that is not a monomer to the solvent containing metal salt and support materials.
5. The method according to claim 1 , further comprising the step of heating the solvent containing the metal salt, the support materials and the monomer to increase the amount of polymerization of the monomer in the solvent.
6. The method according to claim 1 , further comprising the step of adding a polymerization initiator into the solvent containing the metal salt, the support materials and the monomer to increase the amount of polymerization of the monomer in the solvent.
7. A method for producing a supported catalyst, comprising:
adding a fixing agent to a first solvent containing metal salt of a predetermined metal type and support materials, stirring the first solvent to reduce the metal salt, and then separating out the support materials from the first solvent, wherein the fixing agent is a monomer configured to reduce or precipitate the metal salt;
mixing a portion of the support materials separated out from the first solvent and metal salt of the predetermined metal type into a second solvent; and
adding a fixing agent to the second solvent, stirring the second solvent, and then separating out the support materials from the second solvent; and
calcining the support materials separated out from the second solvent to produce the supported catalyst.
8. The method according to claim 7 , wherein the fixing agent added to the first solvent and the fixing agent added to the second solvent are monomers of a type that can be polymerized in the solvent to form oligomers or polymers, or both.
9. The method according to claim 8 , wherein the monomer added to the first solvent and the monomer added to the second solvent comprise acrylic acid.
10. The method according to claim 9 , wherein the metal salt comprises platinum salt.
11. The method according to claim 7 , further comprising the step of calcining the support materials separated out from the first solvent prior to the step of mixing.
12. A method for producing a supported catalyst, comprising:
adding a first fixing agent to a first solvent containing metal salt of a first metal type and support materials, stirring the first solvent to reduce the metal salt, and then separating out the support materials from the first solvent;
mixing a portion of the support materials separated out from the first solvent and metal salt of a second metal type that is different from the first metal type into a second solvent; and
adding a second fixing agent to the second solvent, stirring the second solvent, and then separating out the support materials from the second solvent; and
calcining the support materials separated out from the second solvent to produce the supported catalyst,
wherein at least one of the first and second fixing agents comprise a monomer configured to reduce, respectively, the metal salt of the first metal type and the metal salt of the second metal type.
13. The method according to claim 12 , wherein the monomer is of a type that can be polymerized in the solvent to form oligomers or polymers, or both.
14. The method according to claim 12 , wherein the first fixing agent added to the first solvent comprises acrylic acid and the metal salt comprises platinum salt.
15. The method of claim 1 , further comprising precipitating the metal salt while stirring the solvent containing the metal salt, the support materials and the monomer.
16. The method according to claim 12 , wherein the first fixing agent and the second fixing agent are different compounds.
17. The method according to claim 16 , wherein one of the first fixing agent and the second fixing agent comprises acrylic acid.
18. The method according to claim 17 , wherein the other one of the first fixing agent and the second fixing agent comprises ascorbic acid.