Carbonized asphaltene-based carbon-carbon fiber composites
A method of making a carbon binder-reinforced carbon fiber composite is provided using carbonized asphaltenes as the carbon binder. Combinations of carbon fiber and asphaltenes are also provided, along with the resulting composites and articles of manufacture.
1. A method of making a carbon binder-reinforced carbon fiber composite, said method comprising:
(a) providing a carbon fiber;
(b) providing a plurality of isolated asphaltenes dispersed or dissolved in a solvent system;
(c) contacting said carbon fiber with said plurality of isolated asphaltenes dispersed or dissolved in a solvent system to yield a wetted asphaltene and carbon fiber combination;
(d) removing said solvent system from said wetted asphaltene and carbon fiber combination to yield a dried asphaltene and carbon fiber combination; and
(e) carbonizing said asphaltenes in said dried asphaltene and carbon fiber combination to thereby yield said carbon binder-reinforced carbon fiber composite, said composite having an initial true density of at least 1.9 grams/cc,
said method further comprising repeating (c) through (e).
2. The method of claim 1 , wherein the weight ratio of carbon fiber to asphaltene in said wetted carbon fiber is from about 100:1 to about 100:80.
3. The method of claim 1 , wherein said contacting is carried out under ambient temperature.
4. The method of claim 1 , wherein said removing comprises heating said wetted asphaltene and carbon fiber combination to a temperature of from at least about the boiling point of the solvent system up to about 250° C. for a time period of from about 60 to about 1500 minutes.
5. The method of claim 1 , further comprising pressing said wetted asphaltene and carbon fiber combination into a mold before or during said removing.
6. The method of claim 1 , wherein said carbonizing comprises heating said dried asphaltene and carbon fiber combination to a temperature of from about 1500° C. to about 1800° C. over a time period of approximately 24 hours.
7. The method of claim 1 , wherein said composite has an initial average true density of greater than 2 grams/cc.
8. The method of claim 1 , wherein said solvent system comprises a solvent selected from the group consisting of toluene, tetrahydrofuran, terpenes, and mixtures thereof.
9. The method of claim 1 , wherein said carbon fiber is derived from a precursor selected from the group consisting of PAN, pitch, asphalt, phenolic fibers, rayon, cotton, and lignin.