Pinned furnace tubes
In an embodiment of the invention, furnace tubes for cracking hydrocarbons having a longitudinal array of pins having i) a maximum height from 0.5-1.3 cm; ii) a contact surface with the tube, having an area from 0.1%-10% of the tube external surface area iii) a uniform cross section along the length of the pin. (i.e. they are not tapered); and iv) a length to diameter ratio from 1.5:1 to 0.5:1 have an improved heat transfer over bare fins and reduced stress relative to a fined tube.
1. A tube for use in the radiant section of a furnace for cracking hydrocarbons to produce olefins having on its exterior surface a series of pins in one or more linear arrays parallel to the longitudinal axis of the tube, said pins having:
i) a maximum height from 0.8 cm to 1 cm (paragraph 43);
ii) a contact surface with the tube, having an area from 0.1%-10% of the tube external surface area;
iii) a uniform cross section along the length of the pin;
iv) length to diameter ratio from 1.5:1 to 0.5:1;
v) a distance between consecutive pins within a given linear array is from 0.1 to 5 times the diameter of the pin; and
vi) from 2 to 6 linear arrays of pins radially spaced from 180° to 20° apart.
2. The tube according to claim 1 , wherein the pins have a maximum length from 3%-15% of the tube outer diameter.
3. The tube according to claim 2 comprising from about 55 to 65 weight % of Ni; from about 20 to 10 weight % of Cr; from about 20 to 10 weight % of Co; and from about 5 to 9 weight % of Fe and the balance one or more of the trace elements.
4. The tube according to claim 3 further comprising from 0.2 up to 3 weight % of Mn; from 0.3 to 2 weight % of Si; less than 5 weight % of titanium, niobium and all other trace metals; and carbon in an amount of less than 0.75 weight % the sum of the components adding up to 100 weight %.
5. The tube according to claim 2 , comprising from 40 to 65 weight % of Co; from 15 to 20 weight % of Cr; from 20 to 13 weight % of Ni; less than 4 weight % of Fe and the balance of one or more trace elements and up to 20 weight % of W the sum of the components adding up to 100 weight %.
6. The tube according to claim 5 , further comprising from 0.2 up to 3 weight % of Mn; from 0.3 to 2 weight % of Si; less than 5 weight % of titanium, niobium and all other trace metals; and carbon in an amount of less than 0.75 weight %.
7. The tube according to claim 2 , comprising from 20 to 38 weight % of chromium from 25 to 48, weight % of Ni.
8. The tube according to claim 7 , further comprising from 0.2 up to 3 weight % of Mn, from 0.3 to 2 weight % of Si; less than 5 weight % of titanium, niobium and all other trace metals; and carbon in an amount of less than 0.75 weight % and the balance substantially iron.
9. The tube according to claim 3 , wherein the cross section of the pin is round.
10. The tube according to claim 5 , wherein the cross section of the pin is round.
11. The tube according to claim 7 , wherein the cross section of the pin is round.
12. The tube according to claim 4 , wherein the cross section of the pin is round.
13. The tube according to claim 3 , wherein the cross section of the pin is quadrilateral.
14. The tube according to claim 5 , wherein the cross section of the pin is quadrilateral.
15. The tube according to claim 7 , wherein the cross section of the pin is quadrilateral.
16. The tube according to claim 4 , wherein the cross section of the pin is quadrilateral.
17. Tube according to claim 2 , wherein the pins in a linear array are of uniform height.
18. The tube according to claim 2 , where in the spacing between pins in a linear array is from 0.5 to 5 times the diameter of the pin.
19. The tube according to claim 2 , wherein the pins in a linear array are of different heights to provide a profile to the array.
20. The tube according to claim 19 , wherein at least part of the profile is a taper.
21. The tube according to claim 2 , where in the central axis of the pin is at an angle from 90° to 60° relative to the external surface of the tube.
22. A method for making a tube according to claim 1 , electrically welding a strip of any stud shaped material to the surface of the tube and then cutting the strip at the desired length.