Catalyst layer composition for fuel cell, electrode for fuel cell, method of preparing electrode for fuel cell, membrane-electrode assembly for fuel cell, and fuel cell system using the membrane-electrode assembly

1. A catalyst layer composition for a fuel cell, comprising

an ionomer cluster;

a catalyst adsorbed on the surface of the ionomer cluster;

the ionomer cluster has a three-dimensional reticular structure and a maximized interface with the catalyst and has an average size ranging from about 150 nm to about 250 nm; and

the catalyst is comprised in an amount ranging from about 125 parts to about 250 parts by weight based on 100 parts by weight of the ionomer cluster.

2. The catalyst layer composition for a fuel cell of claim 1 , wherein the ionomer cluster comprises a proton conductive polymer having a cation exchange group selected from a sulfonic acid group, a carboxylic acid group, a phosphoric acid group, a phosphonic acid group and a derivative thereof, at a side chain of the ionomer cluster as a binder.

3. The catalyst layer composition for a fuel cell of claim 2 , wherein the proton conductive polymer comprises a fluorine-based polymer, a benzimidazole-based polymer, a polyimide-based polymer, a polyetherimide-based polymer, a polyphenylenesulfide-based polymer, a polysulfone-based polymer, a polyethersulfone-based polymer, a polyetherketone-based polymer, a polyether-etherketone-based polymer, a polyphenylquinoxaline-based polymer, or combinations thereof.

4. The catalyst layer composition for a fuel cell of claim 2 , wherein the proton conductive polymer comprises poly(perfluorosulfonic acid); poly(perfluorocarboxylic acid); a copolymer of tetrafluoroethylene having a sulfonic acid group and fluorovinylether; defluorinated polyetherketone sulfide; aryl ketone; poly (2,2′-(m-phenylene)-5,5′-bibenzimidazole); poly (2,5-benzimidazole), or combinations thereof.

5. The catalyst layer composition for a fuel cell of claim 2 , wherein hydrogen in the cation exchange group positioned at a side chain of the proton conductive polymer is substituted with Na, K, Li, Cs, or tetrabutylammonium.

6. The catalyst layer composition for a fuel cell of claim 1 , wherein the ionomer cluster is used with a non-conductive compound, and the non-conductive compound comprises polytetrafluoroethylene, a tetrafluoroethylene-hexafluoropropylene copolymer, a tetrafluoroethylene-perfluoroalkylvinylether copolymer, an ethylene-tetrafluoroethylene copolymer, an ethylene-chlorotrifluoroethylene copolymer, a polyvinylidenefluoride, polyvinylidenefluoride-hexafluoropropylene copolymer, dodecylbenzenesulfonic acid, sorbitol, or combinations thereof.

7. The catalyst layer composition of claim 1 , wherein the polyhydric alcohol comprises C 1 to C 6 alkane substituted with 2 to 4 hydroxy groups, C 1 to C 6 haloalkane substituted with 2 to 4 hydroxy groups, or combinations thereof.

8. The catalyst layer composition for a fuel cell of claim 1 , wherein the polyhydric alcohol comprises 1,2-ethanediol, 1,2-propanediol, 1,3-propanediol, 3-chloro-1,2-propanediol, 2-chloro-1,3-propanediol, dipropylene glycol, glycerine, or combinations thereof.

9. An electrode for a fuel cell comprising:

an electrode substrate;

a catalyst layer disposed on the electrode substrate; and

wherein the catalyst layer comprises an ionomer cluster having a three-dimensional reticular structure; and a catalyst adsorbed on the surface of the ionomer cluster.

10. A method of fabricating an electrode for a fuel cell comprising:

preparing an ionomer solution by dissolving an ionomer powder in polyhydric alcohol;

adding a catalyst to the ionomer solution;

preparing a catalyst layer composition of claim 1 by adding water to the ionomer solution comprising the catalyst;

coating the catalyst layer composition on an electrode substrate; and

vacuum-drying the coated electrode substrate to form a catalyst layer on the electrode substrate.

11. The method of fabricating an electrode for a fuel cell of claim 10 , wherein the water is comprised in an amount of about 20 volume % to about 60 volume % based on the total amount of the water and the polyhydric alcohol.

12. The method of fabricating an electrode for a fuel cell of claim 10 , wherein the drying is performed at a temperature ranging from about 50° C. to about 100° C.

13. The method of fabricating an electrode for a fuel cell of claim 10 , wherein the drying is performed under a vacuum degree ranging from about 10 torr to about 760 torr.

14. The method of fabricating an electrode for a fuel cell of claim 10 , wherein the drying is performed for about 1 hour to about 3 hours.

15. A membrane-electrode assembly for a fuel cell comprising:

an anode and a cathode facing each other;

a polymer electrolyte membrane interposed between the cathode and the anode; and

wherein the cathode and the anode respectively are formed of an electrode for a fuel cell of claim 9 .

16. A fuel cell system comprising:

at least one electrical generating element comprising

the membrane-electrode assembly for a fuel cell of claim 15 ;

separators positioned at each side of the membrane-electrode assembly;

a fuel supplier for supplying the fuel to the electrical generating element; and

an oxidant supplier for supplying the oxidant to the electrical generating element.

17. The catalyst layer claim 9 , comprising a composition wherein:

the ionomer cluster has an average size ranging from about 100 nm to about 300 nm, and

the ionomer cluster comprises a proton conductive polymer having a cation exchange group selected from a sulfonic acid group, a carboxylic acid group, a phosphoric acid group, a phosphonic acid group and a derivative thereof, at a side chain of the ionomer cluster as a binder.