A process for the preparation of an object, supporting a lipid bilayer, for use in tissue engineering including the steps of providing an object having a surface, treating the surface of the object with a plasma containing active oxygen to provide the surface of the object with reactive groups A, to provide the surface of the object with reactive groups A, covalently attaching a sterol group to the reactive groups A and contacting the object activated with sterol groups with a lipid solution to form a lipid bilayer.
1. A process for the preparation of an object, supporting a lipid bilayer, comprising the steps of:
providing an object having a surface,
treating the surface of the object with a plasma containing active oxygen to provide the surface of the object with reactive groups A,
covalently attaching a sterol group to the reactive groups A and
contacting the object activated with sterol groups with a lipid solution to form a lipid bilayer.
2. The process according to claim 1 , wherein the object is made of a metal, metal oxides, alloy, glass, ceramic or polymeric materials or combinations of these materials.
3. The process according to claim 1 , wherein an oxygen containing RF plasma or cold plasma is used.
4. The process according to claim 1 , wherein the reactive groups A are aldehyde groups.
5. The process according to claim 1 , wherein the attaching of the sterol groups occurs within 2 hours from treatment of the surface of the substrate.
6. The process according to claim 1 , wherein the sterol group comprises a spacer moiety, which spacer moiety reacts covalently with the reactive groups A on the surface of the object.
7. The process according to claim 6 , wherein the spacer moiety comprises oligo(ethyleneglycol).
8. The process according to claim 1 , wherein the amount of sterol groups attached to the object is between 0.02 nm −2 and 5 nm −2 determined by X-ray photoelectron spectroscopy (XPS).
9. The process according to claim 1 , wherein the lipid solution comprises a phosphatidylcholine derivative.
10. The process according to claim 1 , wherein the lipid bilayer is contacted with a peptide comprising at least one hydrophobic tail.
11. The process according to claim 10 , wherein the peptide is RGD or PHSRN.
12. The process according to claim 1 , comprising the steps of:
a. providing the object from polycaprolactone having a surface,
b. treating the surface of the object with an oxygen containing RF plasma or cold plasma to provide the surface of the object with reactive groups A,
c. reacting the sterol group comprising a cholesterol covalently attached to an oligo(ethyleneglycol) spacer with reactive group A,
d. contacting the object activated with cholesterol groups with the lipid solution comprising a phosphatidylcholine derivative to form the lipid bilayer, and
e. contacting the lipid bilayer with a peptide RGD or PHSRN comprising one or two palmitoyl hydrophobic tails.
13. An object supporting a lipid bilayer, comprising:
an object comprising a polymeric material,
sterol groups covalently attached via a spacer to the polymeric material,
a lipid bilayer surrounding the sterol groups that are covalently attached to the polymeric material and
peptides comprising at least one hydrophobic tail attached to the lipid bilayer.
14. The object according to claim 13 , wherein the polymeric material is a polyester, and wherein the spacer comprises an oligo(ethyleneglycol).
15. The object according to claim 13 , wherein the lipid bilayer comprises DOPC and the peptide is RGD or PHSRN.
16. The object according to claim 14 , wherein the polymeric material is polycaprolactone.