Method for processing a structured surface of an embossing tool
The invention relates to a method for processing a structured surface of an embossing tool, in which the entire surface is provided with a first metallic coating and said surface having, in selected regions, at least one additional metallic coating that has a differing degree of lustre. To improve the optical properties of the material boards produced using the embossing tools, particularly if reproducing a wood texture, the invention suggests that additional differing degrees of lustre should be produced in multiple selected regions on the first coating, and be produced by a combination of metallic coatings and mechanical or chemical after-treatments. Therefore, for example, a wood pore with a defined structure can be substantially better reproduced, and the optical and haptic properties of the wood composite board produced using the press plates can thus be improved.
1. A method for processing a surface of an embossing tool, in which at least one surface is subjected to a first treatment step in the form of a metallic coating, a mechanical gloss-changing treatment or a chemical treatment over the entire area to achieve a degree of gloss and there is at least one further step in selected areas ( 7 , 8 , 9 , 10 , 11 ) to achieve at least one further different degree of gloss,
characterized in that
the at least one further different degree of gloss is obtained in several selected areas ( 7 , 8 , 9 , 10 , 11 ) on the surface with the first degree of gloss, wherein the at least one further degree of gloss is obtained via a metallic coating, mechanical follow-up treatment or chemical follow-up treatment, wherein a protective layer is at least partially applied to the surface by means of a digital printing technique to establish the selected areas ( 7 , 8 , 9 , 10 , 11 ), and wherein the protective layer is applied in a partially overlapping form with respect to the areas that have already been completed.
2. A method according to claim 1 ,
characterized in that
the further degrees of gloss of the surface have at least partially a spacing between them.
3. A method according to claim 1 ,
characterized in that
a material that is resistant to etching, sandblasting or polishing is used for the protective layer.
4. A method according to claim 1 ,
characterized in that
a chromium coating is applied to the surface or the further degrees of gloss of the surface are obtained by etching or sandblasting.
5. A method according to claim 1 ,
characterized in that
the further degrees of gloss of the surface are obtained by mechanical polishing or electropolishing.
6. A method according to claim 1 ,
characterized in that
the surface is activated before the first treatment step or a chromium plating is applied to the surface after the production of the last further degree of gloss.
7. A method for processing a surface of an embossing tool, in which at least one surface is subjected to a first treatment step in the form of a metallic coating or a chemical treatment over the entire area to achieve a degree of gloss and there is at least one further step in selected areas to achieve at least one further different degree of gloss,
characterized in that
the at least one further different degree of gloss is obtained in several selected areas on the surface with the first degree of gloss, wherein the at least one further degree of gloss is obtained via a metallic coating, mechanical follow-up treatment or chemical follow-up treatment and wherein a protective layer is applied in a partially overlapping form with respect to the areas that have already been completed.