Optical glass, optical glass blank, glass material for press molding, optical element, and methods for producing them
An aspect of the present invention relates to optical glass, wherein, in a glass composition based on oxides, a content of P 2 O 5 is in the range of 20˜34 weight %; a content of B 2 O 3 is over 0 weight % but 10 weight % or less; a weight ratio (B 2 O 3 /P 2 O 5 ) is over 0 but less than 0.39; a weight ratio [TiO 2 /(TiO 2 +Nb 2 O 5 +WO 3 +Bi 2 O 3 +Ta 2 O 5 )] is in the range of 0.059˜0.180; and a weight ratio [(P 2 O 5 +B 2 O 3 +SiO 2 )/(Na 2 O+K 2 O+Li 2 O)] is in the range of 1.39˜1.80, the optical glass having a refractive index nd of 1.78˜1.83, and an Abbe's number vd of 20˜25.
1. Optical glass, wherein, in a glass composition based on oxides,
a content of P 2 O 5 is in the range of 20-34 weight %;
a content of B 2 O 3 is over 0 weight % but 10 weight % or less;
a content of Al 2 O 3 is less than 3 weight %;
a weight ratio (B 2 O 3 /P 2 O 5 ) is over 0 but less than 0.39;
a weight ratio [TiO 2 /(TiO 2 +Nb 2 O 5 +WO 3 +Bi 2 O 3 +Ta 2 O 5 )] is in the range of 0.10-0.180; and
a weight ratio [(P 2 O 5 +B 2 O 3 +SiO 2 )/(Na 2 O+K 2 O+Li 2 O)] is in the range of 1.39-1.80,
the optical glass having a refractive index nd of 1.78-1.83, and an Abbe's number vd of 20-25.
2. The optical glass of claim 1 , wherein a weight ratio [SiO 2 /(SiO 2 +P 2 O 5 +B 2 O 3 )] is 0.12 or less.
3. The optical glass according to claim 1 , wherein a content of Li 2 O is 0 weight % or more but less than 0.3 weight %.
4. The optical glass according to claim 1 , wherein a weight ratio [Li 2 O/(Na 2 O+K 2 O+Li 2 O] is less than 0.0115.
5. The optical glass according to claim 1 , wherein a weight ratio [(P 2 O 5 +B 2 O 3 +SiO 2 )/(TiO 2 +Nb 2 O 5 +WO 3 +Bi 2 O 3 +Ta 2 O 5 )] is 0.49 or more.
6. The optical glass according to claim 1 , wherein it has a liquidus temperature of 1050° C. or less.
7. An optical element blank which is comprised of the optical glass according to claim 1 .
8. A method of manufacturing an optical element, comprising a step of grinding and/or polishing the optical element blank of claim 7 to fabricate an optical element.
9. A glass material for press molding, which is comprised of the optical glass according to claim 1 .
10. A method of producing an optical element blank, comprising a step of press molding the glass material for press molding of claim 9 with a press mold to fabricate an optical element blank.
11. A method of producing an optical element, comprising a step of: press molding the glass material for press molding of claim 9 with a press mold to fabricate an optical element.
12. An optical element which is comprised of the optical glass according to claim 1 .
13. A method for producing a glass material for press molding, comprising a step of molding the optical glass according to claim 1 into a glass material for press molding.
14. Optical glass, wherein, in a glass composition based on oxides,
P 2 O 5 , B 2 O 3 and TiO 2 are essential components, and SiO 2 , Li 2 O, Nb 2 O 5 , WO 3 , Bi 2 O 3 , and Ta 2 O 5 are optional components;
a content of P 2 O 5 is in the range of 20-34 weight %;
a content of B 2 O 3 is over 0 weight % but 10 weight % or less;
a content of Li 2 O is 0 weight % or more but less than 0.3 weight %;
a content of Al 2 O 3 is 2 weight % or less;
a weight ratio (B 2 O 3 /P 2 O 5 ) is over 0 but less than 0.39;
a weight ratio [(P 2 O 5 +B 2 O 3 )/(TiO 2 +Nb 2 O 5 +WO 3 +Bi 2 O 3 +Ta 2 O 5 )] is over 0.53; and
a weight ratio [TiO 2 /(TiO 2 +Nb 2 O 5 +WO 3 +Bi 2 O 3 +Ta 2 O 5 )] is in the range of 0.059-0.96,
the optical glass having a refractive index nd of 1.78-1.83, and an Abbe's number vd of 20-25.
15. The optical glass of claim 14 , wherein a weight ratio [SiO 2 /(SiO 2 +P 2 O 5 +B 2 O 3 )] is less than 0.02.
16. The optical glass according to claim 14 , wherein it has a liquidus temperature of 1050° C. or less.
17. The optical glass according to claim 14 , wherein a content of Nb 2 O 5 is in the range of 19-47 weight %.
18. The optical glass according to claim 14 , wherein a content of TiO 2 is in the range of 6-24 weight %.
19. The optical glass according to claim 14 , wherein a content of alkali metal oxide is in the range of 10-30 weight %.
20. The optical glass according to claim 14 , wherein a content of Na 2 O is in the range of 0-16 weight %, and a content of K 2 O is in the range of 0-6 weight %.
21. The optical glass according to claim 14 , wherein a content of Bi 2 O 3 is in the range of 0-15 weight %.
22. The optical glass according to claim 14 , wherein a content of WO 3 is in the range of 0-15 weight %.
23. Optical glass, wherein, in a glass composition based on oxides,
P 2 O 5 , B 2 O 3 and TiO 2 are essential components, and SiO 2 , Li 2 O, Nb 2 O 5 , WO 3 , Bi 2 O 3 , and Ta 2 O 5 are optional components;
a content of P 2 O 5 is in the range of 20-34 weight %;
a content of B 2 O 3 is over 0 weight % but 10 weight % or less;
a content of Li 2 O is 0 weight % or more but less than 0.3 weight %;
a content of Al 2 O 3 is 2 weight % or less;
a weight ratio (B 2 O 3 /P 2 O 5 ) is over 0 but less than 0.39;
a weight ratio [(P 2 O 5 +B 2 O 3 +SiO 2 )/(TiO 2 +Nb 2 O 5 +WO 3 +Bi 2 O 3 +Ta 2 O 5 )] is over 0.53;
a weight ratio [SiO 2 /(SiO 2 +P 2 O 5 +B 2 O 3 )] is less than 0.02; and
a weight ratio [TiO 2 /(TiO 2 +Nb 2 O 5 +WO 3 +Bi 2 O 3 +Ta 2 O 5 )] is in the range of 0.059-0.96,
the optical glass having a refractive index nd of 1.78-1.83, and an Abbe's number vd of 20-25.
24. Optical glass comprising, in a glass composition based on oxides,
24-34 weight % of P 2 O 5 ;
over 0 weight % but 4 weight % or less of B 2 O 3 ;
12-20 weight % of a total of Li 2 O, Na 2 O and K 2 O;
15-30 weight % of Nb 2 O 5 ;
8-15 weight % of TiO 2 ; and,
4-25 weight % of Bi 2 O 3 ,
wherein a weight ratio (TiO 2 /Nb 2 O 5 ) is in the range of 0.36-1.00, and a weight ratio (Bi 2 O 3 /Nb 2 O 5 ) is in the range of 0.16-1.67,
the optical glass having a refractive index nd of 1.78 or greater but less than 1.83, and an Abbe's number vd of 20-25.
25. The optical glass of claim 24 , wherein a total content of Li 2 O, Na 2 O, K 2 O, MgO, CaO, SrO and BaO is in the range of 12-17 weight %.
26. The optical glass according to claim 24 , wherein a weight ratio (B 2 O 3 /P 2 O 5 ) is in the range of over 0 but 0.1 or less.
27. The optical glass according to claim 24 , wherein a weight ratio (WO 3 /Nb 2 O 5 ) is in the range of 0.12-0.92.
28. The optical glass according to claim 24 , wherein a content of WO 3 is in the range of 3-23 weight %.
29. The optical glass according to claim 24 , wherein a content of CaO is less than 1 weight %.
30. The optical glass according to claim 24 , wherein a total content of MgO, CaO, SrO, and BaO is less than 2 weight %.
31. The optical glass according to claim 24 , wherein it has a glass transition temperature Tg of 520° C. or less.
32. A preform for precision press molding, which is comprised of the optical glass according to claim 24 .
33. A method for producing an optical element, comprising a step of: softening the preform for precision press molding of claim 32 under heat and precision-press molding the soften preform with a press mold to fabricate an optical element.
34. An optical element which is comprised of the optical glass according to claim 24 .