1. A method of fabricating a transient semiconductor based on a single-wall nanotube, the method comprising:

(a) stacking a thermal oxide layer on a silicon substrate and depositing a nickel thin layer on the thermal oxide layer;

(b) depositing an oxide layer on the nickel thin layer through a plasma enhanced chemical vapor deposition scheme;

(c) depositing a metallic layer on the oxide layer through an electron-beam deposition scheme, and patterning the metallic layer through a photolithography scheme to form a gate electrode;

(d) depositing a gate insulating layer on the gate electrode through the plasma enhanced chemical vapor deposition scheme;

(e) changing a surface of the gate insulating layer into a hydrophilic surface through plasma treatment or ultraviolet ozone treatment, and washing and drying the gate insulting layer;

(f) coating a single-wall nanotube on the hydrophilic surface of the gate insulating layer;

(g) forming source and drain electrodes by forming a contact opening through a reactive ion etching scheme for the gate insulating layer;

(h) attaching a thermal release tape after removing a surrounding single-wall nanotube through the reactive ion etching scheme;

(i) performing a transfer onto a polyvinyl alcohol thin layer after etching the nickel thin layer using an iron chloride solution; and

(j) releasing the thermal release tape on a thermal plate.

2. The method of claim 1 , wherein the coating of the single-wall nanotube on the hydrophilic surface of the gate insulating layer comprises:

pressing a tape having a circuit on an opposite surface of the polyvinyl alcohol thin layer; and

coating polymethylmethacrylate (PDMS) onto a glass slide.

3. The method of claim 1 , wherein, in the coating of the single-wall nanotube on the hydrophilic surface of the gate insulating layer, a nanowire having a one-dimensional structure and a semiconductor characteristic is coated instead of the single-wall nanotube.

4. The method of claim 1 , wherein the nickel thin layer has a thickness in a range of 250 nm to 350 nm.

5. The method of claim 1 , wherein the forming of the source and drain electrodes by forming the contact opening through the reactive ion etching scheme for the gate insulating layer comprises:

applying a poly-L-lysine solution;

exposing the surface of the gate insulating layer to oxygen gas plasma;

performing a continuous washing process using deionized water; and

performing a drying process under a stream of nitrogen gas.

6. The method of claim 1 , further comprising:

performing a re-washing process using deionized water and isopropyl alcohol; and

performing a re-drying process under a stream of nitrogen gas,

between the coating of the single-wall nanotube and the forming of the source and drain electrodes.

7. The method of claim 1 , wherein the source and drain electrodes include one of a molybdenum layer, a tungsten layer, and a polyethylene dioxythiophene layer.

8. The method of claim 1 , wherein the attaching of the thermal release tape after removing the surrounding single-wall nanotube through the reactive ion etching scheme comprises primarily coating an insoluble polymer buffer layer before attaching the thermal release tape.

9. The method of claim 1 , wherein the polyvinyl alcohol thin layer includes polyvinyl alcohol having a molecular weight in a range of 10,000 to 31,000.

10. The method of claim 9 , wherein the polyvinyl alcohol thin layer is formed by:

dissolving the polyvinyl alcohol having the molecular weight in pure deionized water;

cooling a solution having the dissolved polyvinyl alcohol to a room temperature to extract the solution;

containing the extracted solution to a predetermined initial height in a plastic container;

removing bubbles from the solution having the dissolved polyvinyl alcohol through pumping after placing the plastic container into a vacuum container; and

removing moisture from a bubble-removed polyvinyl alcohol solution using a convection oven or the thermal plate.

11. The method of claim 1 , wherein, in the performing of the transfer onto the polyvinyl alcohol thin layer after etching the nickel thin layer using the iron chloride solution, the transfer is performed using one of poly lacticco-glycolic acid, copolymer of poly lactic acid, poly glycolic acid, and polycaprolactone instead of polyvinyl alcohol.

12. The method of claim 10 , wherein the convection oven or the thermal plate has a temperature in a range of 50° C. to 80° C.

13. The method of claim 1 , wherein the gate insulating layer comprises a double-insulating layer or a single insulating layer.

14. The method of claim 13 , wherein the double insulating layer is formed by sequentially depositing a silicon nitride layer having a thickness in a range of 40 nm to 60 nm and a silicon oxide layer having a thickness in a range of 20 nm to 40 nm.