Coating composition for electrical conductors and method of producing such a composition
The aim of the invention is to create a composition for coating electric conductors which is significantly more resistant to partial discharges than prior art compositions while the produced insulating layer is highly extensible. Said aim is achieved by a composition comprising 1 to 50 percent by weight of microparticles that have a specifically adjusted electronic defect structure in the crystal lattice, resulting in greater polarizability of the valence electrons, and an organic and/or organic-inorganic matrix. The microparticles that have a specifically adjusted electronic defect structure are composed of oxides, sulfides, selenides, tellurides of the elements which are part of the series encompassing silicon, zinc, aluminum, tin, boron, germanium, gallium, lead, the transition metals, lanthanides, and actinides, particularly from the series encompassing silicon, titanium, zinc, yttrium, cerium, vanadium, hafnium, zirconium, nickel, and/or tantalum, in such a way that the basic lattice is provided with vacant lattice positions by doping 4 the basic lattice with adequate low-valent or higher-valent elements, said vacant lattice positions increasing the electronic polarizability of the microparticles by means of defect chemistry (the defect structure).
1. A coating composition for electrical conductors, consisting of
1-50 wt. % of microparticles with a selectively adjusted electronic defect structure in the crystal lattice, said defect structure making the valence electrons more easily polarizable, and
an organic and/or organic-inorganic electrically-isolating polymeric matrix,
the microparticles with the selectively adjusted electronic defect structure being made up of zirconium dioxide in such manner that via doping with yttrium the basic crystal lattice is provided with vacancies which, by way of defect chemistry (defect structure), make it easier for the microparticles to be electronically polarized, wherein the yttrium doping is present in an amount of at least 0.5 mol. % and less than 8 mol. %; and
wherein the organic and/or organic-inorganic matrix includes one or more polymerizable and/or hybrid binders;
wherein the microparticles contain reactive surface groups adapted to the polymer-based and/or hybrid binders; and
wherein said composition contains organically modified inorganic condensates.
2. The composition according to claim 1 , wherein the reactive surface groups are selected from the group comprising metal acid esters, cyanate groups, urethane groups, epoxide groups, epoxy, carboxylic acid anhydride, C═C double bond systems, hydroxyl groups, alcohols bound by way of oxygen, esters, ethers, chelating agents, carboxyl groups, amino groups, ammonium and/or reactive resin components, the polymer-based binders containing acrylate groups, phenol groups, melamine groups, polyester-polyester imide groups, polysulfide groups, epoxide or polyamide groups, polyvinyl formal resins, aromatic compounds, aliphatic compounds, esters, ethers, alcoholates, fats or chelating agents.
3. The composition according to claim 1 , wherein said composition contains one or more of the substances from the group consisting of additives, polymerization initiators, solvents, pigments and/or fillers.
4. The composition according to claim 1 , wherein the average particle diameter of the microparticles with an electronic defect structure is 1-1,000 nm.
5. The composition according to claim 1 , wherein said composition is transparent.
6. The composition according to claim 1 , wherein said composition contains a fluorine compound.
7. The composition according to claim 1 , wherein said composition contains a fluorinated silane, its pre-condensate or condensate.
8. A combination comprising an electrical conductor with
the coating composition according to claim 1 applied to said electrical conductor.
9. A method for coating an electrical conductor comprising the steps of
providing an electrical conductor, and
applying to said electrical conductor the coating composition according to claim 1 .