Method of manufacturing glassine paper

1. A method of manufacturing glassine paper comprising following successive steps of producing paper in a paper machine by forming a paper web in a forming section of the paper machine and drying the web in a press section of the paper machine and in a pre-drying section of the paper machine; applying film-forming product on both sides of the web in the paper machine; removing moisture from the film-forming product applied to the web in an after-drying section of the paper machine wherein moisture CD profile of the web is controlled by transferring heat adjustably in a CD direction while drying the web; passing the web having film-forming product through an on-line calendering process in a calendering treatment section of the paper machine, the on-line calendaring process comprising successive nips in at least one multi-nip calender where the CD thickness profile of the web is controlled and a density and a transparency of the web is increased; and reeling up the glassine paper in a reel-up of the paper machine.

2. A method of manufacturing glassine paper according to claim 1 , wherein the online calendering process comprises at least a first calendering treatment in a first calendering section and a second calendering treatment in a second calendering section.

3. A method of manufacturing glassine paper according to claim 2 , wherein the online calendering process further comprises controlling web tension between the first and the second calendering treatment.

4. A method of manufacturing glassine paper according to claim 2 , wherein the first calendering treatment comprises treating the paper web in at least four successive calendering nips.

5. A method of manufacturing glassine paper according to claim 2 , wherein the second calendering treatment comprises treating the paper web in at least two successive calendering nips.

6. A method of manufacturing glassine paper according to claim 1 , wherein the online calendering process comprises application of water by condensing steam onto the web before passing the web to the calendering treatment section.

7. A method of manufacturing glassine paper according to claim 1 , wherein the online calendering process comprises cooling the paper web and application of water by condensing steam onto the web before passing the web to the calendering treatment section.

8. A method of manufacturing glassine paper according to claim 1 , wherein removing moisture from the film-forming product applied to the web in the after-drying section comprises a step of controlling moisture CD profile of the web by transferring heat adjustably in CD direction while drying the web; and wherein controlling moisture CD profile is based on a moisture content profile of the web entering the calendering treatment section.

9. A method of manufacturing glassine paper according to claim 1 , wherein drying the web in the pre-drying section and applying film-forming product on both sides of the web comprises a step of controlling moisture CD profile of the web by transferring heat adjustably in CD direction to the web at the press section; and wherein controlling moisture CD profile is based on a moisture content profile of the web.

10. A method of manufacturing glassine paper according to claim 9 , wherein drying the web in the press section comprises a step of controlling moisture CD profile of the web by transferring heat adjustably in CD direction to the web prior to entering into a press nip; and wherein controlling moisture CD profile is based on a moisture content profile of the web before applying film-forming product on both sides of the web.

11. A method of manufacturing glassine paper according to claim 1 , wherein drying the web in the press section comprises a step of controlling moisture CD profile of the web by transferring heat adjustably in CD direction to the web prior to entering into a press nip; and wherein controlling moisture CD profile is based on a moisture content profile of the web before applying film-forming product on both sides of the web.

12. A method of manufacturing glassine paper according to claim 1 , wherein the calendering treatment section comprises heating cylinders, the heating cylinders defining nips, and wherein a temperature of the heating cylinders are controlled to be 170-240° C., and a nip load of the calendering treatment section is controlled to be 270-400 kN/m.

13. A method of manufacturing glassine paper according to claim 1 , wherein a target calendering process moisture content is set for the web and wherein the target calendering process moisture content of the web is achieved by drying the web in the after-drying section.

14. A method of manufacturing glassine paper according to claim 13 , wherein the after-drying section is operated so that the target calendering process moisture content is obtained by increasing web moisture content up to a point where the target moisture content is achieved.

15. A method of manufacturing glassine paper according to claim 14 , wherein the web is further dried in a post-calendering drying section resulting in a final moisture content.

16. A method of manufacturing glassine paper according to claim 14 , wherein the web film-forming product comprises at least one of starch, polyvinyl alcohol, carboxymethyl cellulose, and alginate.

17. A method of manufacturing glassine paper according to claim 13 , wherein the web is further dried in a post-calendering drying section resulting in a final moisture content.

18. A method of manufacturing glassine paper according to claim 17 , wherein in the post-calendering drying section the web is subjected to drying with cylinders having surface roughness selected so that a web surface quality obtained in the preceding calendering process will be remained or improved.

19. A method of manufacturing glassine paper according to claim 1 , wherein the on-line calendering process is performed at elevated moisture content, wherein the elevated moisture content comprises a moisture content wherein the on-line calendering process alone cannot evaporate sufficient water from the web to provide a final moisture content for a commercial product, and wherein the web is further dried in a post-calendering drying section resulting in the final moisture content.

20. A method of manufacturing glassine paper according to claim 1 , wherein the CD thickness profile in the at least one multi-nip calender is controlled by a heat transfer system capable of heating a roll surface locally and in an adjustable manner in the CD direction.